具有阵列-簇双层结构的TiO_2纳米棒的光电性能研究.pdfVIP

第34卷 第 1期 发 光 学 报 Vo1．34 No．1 2013年 1月 CHINESE JOURNALOF LUMINESCENCE Jan．， 2013 ArticleID：1000-7032(2013)01-0061-05 PhotoelectricalPropertiesofTiO2Nanorods withAnArray--clusterDouble--layeredStructure SUNQiong，SUNXian—miao，LIYang，DONGLi—feng， (1．CollegeofMaterialsScienceandEngineering，QingdaoUniversityofScienceandTechnology，Qingdao266042，China 2．DepartmentofPhysics，Astronomy，andMaterialsScience，MissouriStateUniversity，Springfield，M~souri65897，USA) CorrespondingAuthor，E—mail：donglifeng@qust．edu．cn Abstract：Titaniumoxysulfate(TiOSO4)wasusedasaninorganictitaniumprecursortosynthesizeTiO2nanorods onatransparent，conductivefluorine—dopedtinoxide(FTO)substratebyafacilehydrothermalprocess．TheTiO2 nanorodfilm wasrutilephaseandexhibitedanarray—clusterdouble—layeredstructure．Undertheilluminationofaso— larsimulator．theshort—circuitphotocurrentdensityofTiO，nanorodsmaximizedat0．17mA／cm ，whichwasover twicethatofsamplesoriginatingfromorganictitaniumisopropoxide[Ti(iPro)4]underthesameconditions．Multi— dimensionalstructureandtheparticipationofinorganicoxysulfate(OSO：一)anioncontributetotheenhancedphoto— currentresponseofTiO2nanorodfilms． Key words：TiO2nanorod；hydrothermalmethod；morphology；photoelectricalproperty CLC number：0484．4 Documentcode：A DOI：10．3788／fgx0061 具有阵列．簇双层结构的TiO2纳米棒的光电性能 孙 琼 ，孙先淼 ，李 阳 ，董立峰 (1．青岛科技大学 材料科学与工程学院，山东 青岛 266042； 2．美国密苏里州立大学物理、天文与材料科学系，密苏里州 斯普林菲尔德 65897) 摘要：选择硫酸氧钛(Ti0so)作为无机钛源前驱体，通过温和的水热法在掺氟氧化锡导电玻璃基底(fro) 上直接合成单晶金红石相TiO 纳米棒薄膜 ，呈现阵列一簇双层结构。在模拟太阳光照射下，该纳米棒薄膜的 短路电流可达到0．17mA／cm ，是相同条件下由四异丙醇钛 [，Ii(／Pro)]为有机钛源而制备的TiO 纳米棒薄 膜的2倍多。实验结果表明，多维层状结构和无机硫酸氧根离子(os0：一)的存在对TiO 纳米棒薄膜的光电 流响应有促进作用。 关 键 词：TiO2纳