混凝土杨氏模量预测的双夹杂模型研究.pdf

混凝土杨氏模量预测的双夹杂模型1 肖建强 王伟 (南京工程学院建筑工程学院, 南京, 211167) 摘要 本文对混凝土的弹性性质进行了计算，将混凝土简化为由水泥浆、细骨料和粗骨 料所组成的三相复合材料，运用了 Benveniste 对 Mori-Tanaka 法的解释和 Eshelby’s 等 效介质理论对其进行了计算，最后将本文方法所推导出来的理论结果与公开发表的实 验数据进行了比较。 关键词 细观力学，混凝土，杨氏模量 中国分类号 TU528.01 文献标识码 A Double inclusion model for the prediction of young’s modulus of concrete Xiao Jianqiang Wang wei (Institute of Civil Engneering, Nanjing Institute of Technology,Nanjing,211167) Abstract: The elastic properties of concrete is calculated in this paper. The concrete is considered as three-phase composite materials composed with cement paste 、fine aggrerate and coarse aggregate. Two kinds of methods, Benveniste’s explaination for Mori-Tanaka method and Eshelby’s equivalent inclusion theoretical, are used to compute the concrete elastic modulus. Final, the theoretical result deriving from this study is compared with the published experimental data. Key Words: micromechanics; concrete; young’s modulus 1 引言 一般在建立近似估计方法时有三个共同的步骤：（1）复合材料微结构的实验表征和相材 料性质的确定；（2）建立局部化关系；（3）均质化。局部化关系是细观力学近似方法的核心， 其目的是建立复合材料代表单元在均匀边界条件下，代表单元内部各点的应力和应变与所施 加宏观外载的关系。 复合材料的平均弹性模量（体积模量、剪切模量）是细观力学的经典问题之一，W.Voigt [1] [2] （1889） 采用并联模型（基于应变等效）与 Reuss（1929） 采用串联模型（基于应力等 效）研究过此问题，后来 Hill[3]证明 Voigt 的近似与 Reuss 的近似各给出平均模量的上限和 下限，即由满足最小势能原理所构造的均匀应变场推得的有效模量给出平均模量的上限，同 样，由满足最小余能原理所构造的均匀应力场推得的有效模量给出平均模量的下限。 收稿日期：2008 基金项目：南京工程学院科研基金项目（KXJ07018 ） 作者简介：肖建强(1975-)，男，硕士研究生，讲师，主要从事力学教学与科研工作 E-mail: xiaojq7754@ 第 488 页 本文将混凝土这种复合材料考虑为一个三相复合材料，由水泥浆（基体介质）、砂（细 骨料）和砾石（粗骨料）所组成，因此，认为混凝土复合材料的平均弹性性质（剪切模量与 体积模量）与水泥沙浆、细骨料和粗骨料的弹性性质以及所占的体积百分比密切相关。本文 在参考文献[7]的基础上，运用了 Be