水泥助磨剂性能测定方法的试验研究.pdf

2009.No.11 - 1 - 水泥助磨剂性能测定方法的试验研究 王复生 （济南大学 材料科学与工程学院，山东 济南 250022 ） 摘要：研究了三种高效助磨剂对普通硅酸盐水泥性能的影响。结果表明：不同助磨剂对水泥颗粒的粒径分布、筛余、流动 性，尤其是对粒径3～32μm 颗粒的含量以及水泥各龄期强度都有不同的影响。 而对由透气法测得的勃氏比表面积无明 显影响。 水泥助磨剂的性能可用磨制的水泥的颗粒组成、45μm 筛余、流动性、强度来表征或评价。 而勃氏比表面积不适 宜用来表征助磨效果。 同时对助磨剂作用微观机理也进行了探讨。 关键词 水泥；助磨剂；性能 : Abstract: The effect of three types of grinding aids on the performance of ordinary Portland cement was studied. The result showed that with different grinding aids the cement particle size distribution, sieve residues, fluidity of cement particles, especially the content of particles with size of 3-32μm and cement strength in each age would be varied considerably, while it had no obvious effect on specific surface area (Blaine method). The properties of cement grinding aids could be evaluated by cement particles composition, 45μm sieve residues and strength but excluding specific surface area (Blaine method). The micro-mechanism of function of grinding aids was also presented. Key words: cement; grinding aids; performance First authors address: School of Materials Science and Engineering of Jinan University, Jinan 250022, Shandong, China 中图分类号： 文献标识码： 文章编号： （ ） TQ172.463 A 1002－9877 2009 11-0001-04 0 引言 第一组是为了研究不同品种及掺量的助磨剂对硅酸 在水泥生产中，助磨剂的研究与应用受到越来越 盐水泥性能影响的表征方法，掺量分别为M1 0.03% ； ； 。 第二组是对 进行最佳掺量 多的关注。 在助磨剂的试验研究中，研究人员一般是 M2 0.04% M3 0.5% M2 研究（分别为 、