固相含量和分散剂对CLST流延浆料流变性能影响的研究.docVIP

固含量和分散剂对CLST 流变性能影响摘 要 现代移动通信、无线网络等设备正趋向于小型、轻量、多功能及低成本化方向发展，对各种电子元器件提出了更高的要求。为满足此要求，利用低温共烧陶瓷(LTCC)技术设计制造片式多层微波器件已成为当今的研究热点。流延成型工艺因其简单、稳定、产品性能优良的特点，成为电子元件生产的支柱技术，也是LCC技术道工艺流延法通常需要在陶瓷粉料中添加溶剂、分散剂、粘结剂与塑性剂等有机成分制得分散均匀和稳定的料浆稳定均一的浓悬浮体制备是流延成型出密度高且均匀、结构性能优良坯体的前提，而粉体含量和外加剂（如分散剂、粘结剂等）能够显著影响浆料流变性能，对稳定的浓悬浮体的制备有着非常重要的作用本实验的内容是加入不同的分散剂通过旋转粘度计测出相应的粘度来研究分散剂含量对CLST陶瓷流变性能的影响。同样通过改变固含量测出相应粘度来研究不同固含量对CLST陶瓷流变性能的影响。结果表明：一、随着分散剂浓度增加，不同固相体积分数的瓷陶浆料黏度都是先逐渐减小，达到最低值后，又缓慢升高，每个固相体积分数的浆料均存在一个最佳的分散剂用量。二、随着固相体积分数的增加，粘度变大，浆料流动性变差 关键词：流延成型，固含量，分散剂，流变性能，旋转粘度计，CLST陶瓷 Solid Content and Dispersant on Rheologyical Beheavor of CLST Slurry ABSTRACT With the rapid development of mobile telecommunication, wireless local area network(LAN), it has been strongly required that the related components become small sized, light-weighted，multilow cost. In order to fulfill these requirements, design and fabrication of multilayer chip microwave components using. Low Temperature Co-Fired Ceramics (LTCC) technology has been the research focus. Tape casting is the most efficient and reliable method to produce thin ceramic tapes that are necessary for manufacturing multilayer microwave ceramics. Polyvinyl fluorite (PVF) usually need in ceramic，it added solvent, dispersant, adhesive and plasticity agent and so on. It could make the slurry dispersion and stability. It is the preparation for forming high density and uniform structure, good performance green body. Solid content and admixture (such as the content of dispersant binder.) can significantly affect slurry rheological beheavor, They have a very important role for making stability slurry. This experiment content is joined different dispersant in the slurry，Then measure the viscosity by NDJ-79 rotating viscometer, It is the method for measuring the CLST ceramic slurry rheological properties. Through the same method, changing solid content to study different viscosity measure corresponding CLST ceramic rheological beheavor of solid content can influence. Results: First,