高强度宽厚板控冷技术浅析_宽厚板_2009tr.pdfVIP

第15卷第3期 宽厚板 VolJ 15．No．3 · 24‘2009年6月 WIDE AND HEAVY PLATE June 2009 · 技术讨论· 高强度宽厚板控冷技术浅析 肖丰强 候登义 马兴云 (济南钢铁集团有限公司) 摘 要 概述了控制冷却工艺，阐明了控制冷却的实质与机理，介绍了宽度板生产中常用控制冷却方式、 控制冷却技术难点及相应措施。通过典型控制冷却工艺及其工艺参数的分析，对宽厚板生产企业控制冷却技 术的应用与生产工艺方案的制定起到了一定的参考作用。 关键词 宽厚板 控制冷却 工艺参数 Analysis on Controlled Cooling Technique for High Strength Wide and Heavy Plate Xia0 Fengqiang Hou Dengyi and Ma Xingyun ．， (Jinan Iron and Steel Group Co．Ltd) Abstract This paper reviews controlled cooling technology，describes its nature and mechanism，introduces the common controlled cooling mode used in wide and heavy plate production as well as technical difficulties and relevant measures．The discussion on typical controlled cooling technique and the analysis OIl the process parameters provide reference to the wide and heavy plate producer in the application of controlled cooling technique and preparation of pro· duction process plan． Keywords Wide and heavy plate；Controlled cooling，Process parameters 0 前言 的组织和性能。主要途径是：细化铁素体晶粒；增 利用钢板热轧后的余热，进行在线控制冷却， 加贝氏体数量；弥散析出碳、氮化物。控制冷却能 在保证板材要求的板型尺寸规格的同时可控制和 有效防止铁素体晶粒长大，阻止或减少网状碳化 提高板材的综合力学性能 ]。主要是通过控制 物的析出量，保持其碳化物固溶状态，达到固溶强 其相变与碳化物析出，在不降低韧性的条件下提 化之目的，同时减少珠光体球团尺寸，改善珠光体 高强度，在不降低强度的条件下减少碳当量，从而 形貌和片层间距l_2 J。钢从奥氏体转变为铁素体 提高钢材综合性能。除改善钢板性能外，还可免 或珠光体型组织时，是以扩散方式进行的，钢从奥 去轧后淬火或回火等热处理工序，大大降低生产 氏体转变为马氏体或贝氏体组织时，则是以切变 成本。 方式进行的。因此，就相变机理而言，加速冷却工 目前，控制冷却已广泛应用于船板、管线板、 艺主要是利用扩散相变机理和细化晶