低焊接裂纹敏感性钢焊接接头组织及微观力学性能-Journalof.PDFVIP

第32 卷第4期 东 北 大 学 学 报 ( 自 然 科 学 版 ) Vol32, No. 4 2 0 1 1 年 4 月 Journal of Northeastern U ni ersity( Natural Science) Apr. 2 0 1 1 兰亮云, 邱春林, 赵德文, 高秀华 ( , 110819) : , : , , , ; + , , ; : ; ; ; ; : T G 401 : A : 1005-3026( 2011) 04-0505-04 Structure and Micromechanical Properties of a Weld Joint Using Steel with Low Sensitivity to Weld Cracking LAN Liang-yun, QI U Chun-lin, ZHA O De-wen, GA O X iu-hua ( T he State Key Laboratory of Rolling and Automation, Northeastern Uni ersity, Shenyang 110819, China. Corresponding author : LA N Liang-yun, E-mail: lly liangyun @ gmail. com) - Abstract Submerged arc w elding technology was used to w eld a steel plate with low susceptibility to w eld cracking, and microstructure obser ation, con entional Vickers microhardness and nanoindentation examination were conducted in the heat affected zone ( HAZ) . T he results show that a coarse grained HAZ mainly consisted of coarse granular bainite. Ow ing to a large number of nanoprecipitates and higher dislocation density, the higher microhardness and nanohardness were obtained in the coarse grained HAZ. The w eld zone and fine grained HAZ mainly consisted of acicular ferrite plus proeutectoid ferrite and quas-i polygonal ferrite, respecti ely, and their nanohardness and modulus of elasticity w ere both less than that of the coarse grained HAZ. The greatest strength w as obser ed in the coarse grained HAZ. T he coarse granular bainite may diminish impact toughness, causing localized brittle fractures in the head of the coarse grained HAZ. Key words low welding crack susceptibility steel; HAZ; nanohardness; elastic mo