熔融镁-氧化锆共烧耐火材料外文文献.pdfVIP

Ceramics International 43 (2017) 14263–14270 Contents lists available at ScienceDirect Ceramics International journal homepage: /locate/ceramint Fused magnesia-zirconia co-clinker for fired refractories MARK ⁎ Robert Kusiorowski , Bronisław Psiuk Institute of Ceramics and Building Materials, Refractory Materials Division in Gliwice, ul. Toszecka 99, 44-100 Gliwice, Poland A R T I C L E I N F O A B S T R A C T Keywords: In this paper developing a method of obtaining fused magnesia-zirconia co-clinker has been described. The D. MgO fused co-clinker has been prepared from high-purity raw materials in an arc-resistance furnace. The fused D. ZrO2 magnesia-zirconia co-clinker was added to the ceramic mass sets in different amounts. The main properties of E. Refractories the fired samples obtained from fused MgO-ZrO2 co-clinker were compared with samples without any addition of zirconia as well as with materials obtained in the traditional way, i.e. by sintering a mix of magnesia and zirconia. It has been proved that the obtained fused MgO-ZrO2 co-clinker may be treated as a valuable raw material to modify the