SA738Gr_B焊接工艺研究.docx

于立学，宋聚海（山东核电设备制造有限公司，山东 海阳 265118）摘要：结合 ASME 焊接标准和先进压水堆钢制安全壳设计技术要求，对某大型先进压水堆核电站钢制 安全壳用 SA738 Gr.B 钢板进行了热处理工艺条件下和非热处理条件下的焊接工艺性能试验研究。试验 证明，采用的焊材、焊接工艺参数及焊后热处理工艺能够满足 SA738 Gr.B 钢板的焊接成型技术要求。 关键词：大型先进压水堆；安全壳；焊条电弧焊；SA738 Gr.B中图分类号：TG457.11文献标志码：B文章编号：1001－2303（2014）03－0001-04DOI：10.7512/j.issn.1001-2303.2014.03.01Study on the welding procedure of SA738 Gr.BYU Li-xue，SONG Ju-hai（Shandong Nuclear Power Equipment Manufacturing Co.，Ltd.，Haiyang 265118，China）Abstract：Based on ASME welding standard code and the design technique requirement of containment vessel of the advanced-large pressure water nuclear reactor station，The welding procedure of SA738 Gr.B was studied in this paper with heat treatment process and un-heat treatment conditions.Tests show that the welding material，welding variables and heat treatment procedure used in this paper were well meet the welding forming requirements of SA738Gr. B.Key words：advanced-large pressure water nuclear reactor station；containment vessel；SMAW；SA738 Gr. B0前言某大型先进压水堆核电站钢制安全壳在设计 上采用厚度 41～48 mm 的低合金 SA738 Gr.B 钢板。 由于美标 SA738 Gr.B 钢板在中国属于新材料，目前 很少有可借鉴的焊接工艺和方法；另一方面，由于 该安全壳所用钢板材较厚，有一定的焊接技术难 度。本研究在焊条电弧焊（SMAW）焊接方法基础 上，以进行热处理和不进行热处理两种状态进行了 SA738 Gr.B 焊接工艺性试验研究，获得了理想的 试验结果，为该类核电站钢制安全壳的高质量焊接收稿日期：2013－07－13作者简介：于立学（1976—），男，黑龙江绥化人，焊接工程师， 主要从事核电制造焊接方面的工作。成型提供了可靠的技术保障。1试验用材料介绍1.1SA738 Gr.B 钢板SA738 Gr.B 为美国 ASME 规范中的牌号，随着 中国核电技术的引进、消化和再创新，目前国内已经 有少数钢厂掌握了该种钢板的制造生产技术。本实 验研究材料选用国内某钢厂研制的 SA738 Gr.B 钢 板，交货状态为淬火+回火状态，钢板厚度 42.1 mm，主 要化学成分和机械性能见表 1。1.2焊接材料基于焊条电弧焊（SMAW）对 SA738 Gr.B 钢板 进行焊接工艺性试验研究，焊接材料选用某制造商表 1 SA738 Gr.B 化学成分及机械性能w（C）/% w（Mn）/% w（Si）/% w（S）/% w（P）/% w（Cr）/%0.091.320.280.007 3 0.001 10.12w（Ni）/%w（Mo）/%w（V）/%w（Nb）/%w（Nb+V）/%0.390.140.0430.0040.047抗拉强度屈服强度延伸率平均冲击功σb/MPaσs/MPaδ/%Akv/J(-45 ℃)62654725306的 E9018-G-H4R 型号焊条。该焊条具有飞溅少、易 引弧等优良特性。焊条的化学成分和主要机械性能 如表 2 所示。焊条使用前在 350 ℃烘干 2 h，150 ℃ 保温。表 2 E9018-G-H4R 焊条化学成分及机械性能w（C）/%w（Mn）/%w（Si）/%w（S）/%w（P）/%0.051.200.400.0070.015w（Ni）/%w（Mo）/%w（V）/%w（Cu）/%w（Nb）/