第八章-疲劳裂纹扩展2.pptVIP

* * 第八章 疲劳裂纹扩展 8.1 疲劳裂纹扩展速率 8.2 疲劳裂纹扩展寿命预测 8.3 影响疲劳裂纹扩展的若干因素 8.4 疲劳裂纹扩展速率试验 返回主目录 前节回顾: The plot of log da/dN versus log DK is a sigmoidal (S形) curve. This curve may be divided into three regions. At low stress intensities, cracking behavior is associated with threshold effects. In the mid-region, the curve is essentially linear. Finally, at high DK values, crack growth rates are extremely high and little fatigue life is involved. lg da / dN 1 2 3 10 -5 -6 10 -9 lg ( K) D ~ c K =(1- R) ?K=(1-R)Kmax th D K Most of the current application of LEFM concepts to describe crack growth behavior are associated with region 2. In this region the log da/dN versus log DK curve is approximately linear and lies roughly between 10-7 and 10-4 mm/cycle. Many curve fits to this region have been suggested. The Paris equation, which was proposed in the early 1960’s, is the most widely accepted. 大多数用线弹性断裂力学描述裂纹扩展的应用是与区域2相关的。在这一区域，logda/dN - log DK曲线近似线性且在10-7-10-4 mm/c间。已有许多拟合曲线提出，60年代初的Paris公式是应用最广的。 8.3 影响疲劳裂纹扩展的若干因素 ?K是控制da/dN的最主要因素。 平均应力、加载频率、环境等的影响较次要，但有时也不可忽略。 同一材料, 由不同形状、尺寸的试件所得到的da/dN-?K曲线相同。 da/dN-?K曲线可以描述疲劳裂纹扩展性能。 ?K Mpa.m1/2 4 10 20 40 lgda/dN (m/c) -9 -8 -7 -6 碳钢 R=0.05 ?K Mpa.m1/2 1. 平均应力或应力比的影响 注意到 ?a=(1-R)?max/2， ?m=(1+R)?max/2； 有： 故?a 给定时， R ，?m 。 讨论应力比的影响， 就是讨论平均应力的影响。 a m R R s s ) 1 ( ) 1 ( - + = R>0、R<0影响趋势不同。 th K R=0.8 0 -1 lgda/dN D lg( K) D 实验结果 th K R=0.8 0 -1 lgda/dN D lg( K) D R＞0的情况 R>0时，?min>0。 ?a 给定，R ， ?min ， ?max 。 三个速率区域内，da/dN均增大。da/dN-?K 曲线整体向左移动。 Forman公式： K K R K C dN da C m D - - D = ) 1 ( ) ( ?K=(1-R)Kmax Kmax?Kc， 分母?0，da/dN??。 ?K??Kth，da/dN?0。 若考虑?Kth的影响，有： da dN C K K R K K m th m c = - - - [ ( ) ( ) ] ( ) D D D 1 th K R=0.8 0 -1 lgda/dN D lg( K) D 低速率区，R?，?Kth?。 R＜0的情况：负应力存在， 对da/dN三区域的影响不同。 情况比R>0时复杂得多。 0 .2 .4 .6 .8 1.0低碳钢 低合金钢 不锈钢 A517-F 930