Hydrogen Storage Materials 能源教育知識網 Hydrogen Storage Materials energy education knowledge network.pptVIP

Clathrate hydrates H2 caged in a clathrate hydrate was first reported in 2002, but requires very high pressures to be stable. In 2004, researchers from Delft University of Technology and Colorado School of Mines showed solid H2-containing hydrates could be formed at ambient temperature and 10s of bar by adding small amounts of promoting substances such as THF. These clathrates have a theoretical maximum hydrogen densities of around 5 wt% and 40 kg/m3. Glass capillary arrays A team of Russian, Israeli and German scientists have collaboratively developed an innovative technology based on glass capillary arrays for the safe infusion, storage and controlled release of hydrogen in mobile applications. The C.En technology has achieved the United States Department of Energy (DOE) 2010 targets for on-board hydrogen storage systems. Glass microspheres Hollow glass microspheres (HGM) can be utilized for controlled storage and release of hydrogen. Department of Mechanical Engineering, Yuan Ze University * Proposals and research - Chemical storage Metal hydrides Metal hydrides, such as MgH2, NaAlH4, LiAlH4, LiH, LaNi5H6, TiFeH2 and palladium hydride, with varying degrees of efficiency, can be used as a storage medium for hydrogen, often reversibly. Some are easy-to-fuel liquids at ambient temperature and pressure, others are solids which could be turned into pellets. These materials have good energy density by volume, although their energy density by weight is often worse than the leading hydrocarbon fuels. Most metal hydrides bind with hydrogen very strongly. As a result high temperatures around 120 °C (248 °F) – 200 °C (392 °F) are required to release their hydrogen content. This energy cost can be reduced by using alloys which consists of a strong hydride former and a weak one such as in LiNH2, NaBH4 and LiBH4. These are able to form weaker bonds, thereby requiring less input to release stored hydrogen. However if the interaction is too weak, the pressure needed for rehydri