双金属复合管离心铸造凝固过程温度场数值模拟-机械设计及理论专业论文.docxVIP

studied.Moreover，mathematical model of 2D inverse heat conductíon problem was buílt and detailed deduced process and program flow chart are described. The instanceapplication indícates that the progr创n can obtain the unknown boundary heat fluxbased on the finite measured temperature values correctly. Besides，it is introduced to use in calculating the convective heat transfer coefficient between mold and casting. The principle chart of equipment to measure temperature of mold in centrifuga l casting machine was designed . As a result，aforementioned mathematical method can make thesimulation results more close to the reality.Key Words: Centrifuga l Casting; Bi-metal Composite Pipe; Temperature Field ;Numerical Simulation; Inverse Heat Conduction ProblemThesis Type: Application Research目录1. 绪论......................................…....................................................................................11.1 课题来源及研究意义 ...................... ............................ ...................................... ... 11.2 双金属复合 管及其生产工艺概述 ......... ............................................................ 11.3 双金属离心铸造工艺研究现状.......…..............….. ......……......…….......…..…........21.4 离心铸造凝固过程数值模拟研究现状..............................…..… ..........................41.5 课题研究内容及方法.......... .......….......................….............. ......….......….........72. 双液离心浇注士，艺及复合界面结合机理研究........ ..........….......... ........... ..........92.1 复合材料的选材依据.......……................................................. ..............................92.2 双液离心复合工艺方案的确 定 ................... .......................... ........................... 112.2.1 双液离心机工作原理...............…................……….. .....….......….................... 112.2.2 转速的确定.........................…........................…… .........................................132.2.3浇注温度确定.........……........……...............…....................………… ................ 142.2.4时间间隔确定.........