低温胶凝材料的研究.docVIP

低温胶凝材料的研究 随着经济建设的发展,各行业对胶凝材料的要求不仅从数量上而且从质量上提出新的指标。在一些严寒地区，现有的胶凝材料的效果还是不大理想，所以研发在低温严酷环境中发挥作用的胶凝材料势在必行。本文从组成成分，微观面貌，核心技术原理等方面，对目前应用广泛的三种低温胶凝材料进行了分析，为新型低温胶凝材料的研发奠定了基础。 低温条件；胶凝材料；磷石膏；水泥 Study on low temperature cementitious materials Student NoName Ning Sun Student NoName Rui Kang Student NoName Fei Dai Student NoName Xin Jiang With the development of economic construction, the industry puts forward a new index for the quantity and quality of cementitious materials. In the cold area, the existing cementitious material effect is not ideal, so the development of cementitious materials play imperative role in low temperature environment. This article will have carried on the analysis to three kinds of widely used low temperature cementing material from the composition, the micro appearance, the core technology principle and so on, which has laid the foundation for the new low temperature cementing materials research and development. Low temperature condition; Cementing material; Phosphogypsum; Cement1 胶凝材料概念及分类 胶凝材料概念 胶凝材料是指通过自身的物理化学作用，由可塑性浆体变为坚硬石状体的过程中，能将散粒或块状材料粘结成为整体的材料，亦称为胶结材料。 根据化学组成的不同，胶凝材料可分为无机与有机两大类。石灰、石膏、水泥等工地上俗称为 “灰”的建筑材料属于胶凝材料而沥青、天然或合成树脂等属于胶凝材料无机胶凝材料按其硬化条件的水硬性不同又可分为气硬性和两类。 [1] 表1 磷石膏的化学成分 成份 CaSO4 A1203 Fe203 Mg0 Si02 F- P205 有机物 结晶水 烧失量 含量(%) 82.0 0.48 0.46 0.12 4.56 0.57 3.52 1.57 6.35 29.0 2.1 磷石膏研究背景 据了解，全世界磷石膏的年排放量接近2亿吨，这不仅占用大量土地而且严重地污染了环境。这些工业废渣也是可利用的资源，从60年代至今不少国家都在致力于磷石膏的再利用开发工作并且在理论上和实践上都取得了不少的成果。例如日本千叶县磷酸厂利用磷石膏生产建筑用β-半水石膏粉；法国Rhone-pou1enc公司将磷石膏在渣池中经搅拌呈悬浮态完成初洗以除去粗大颗粒和可溶性P205和可溶性杂质；德国Giulini公司利用磷石膏生产α-半水石膏，俄国伏伊瓦尼斯基报道在磷石膏中加水及添加剂，然后在加压反应釜中于 120°C—140°C下脱水生成α-半水石膏经过滤、活化制成料浆并成型制成石膏板。[2] 2.2 低温陶瓷化磷石膏基复合胶凝材料的研究 有研究表明采用添加活化工业矿渣，在硅酸盐、石灰等复合激发剂的共同作用下，充分利用其自身的物性组成及潜在活性。在半水磷石膏水化过程中，选用的激发剂可进一步改善二水磷石膏晶型，同时促进矿渣的水化进程，形成类陶瓷结构的网络组成，与石膏结晶体相互交接在一起，就形成了低温陶瓷化的磷石膏基复合胶凝材料。 2.2.1 核心技术原理 根据不同工艺条件，二水石膏脱水可得α型半水石膏(α一hemihydrate Gypsum)或β型半水石膏(β—hemihydrate Gypsum)两种半水石膏变体。当二水石膏在饱和水蒸汽条件，或在酸、盐的溶液中加热脱水，即可形成α一半水石膏；如果在缺少水蒸汽的干燥环境中脱水则形成β一半水石膏