毕业设计说明书课 题：箱体的加工工艺及夹具设计 专 业 机械制造与自动化 学生姓名 班 组 学 号 指导教师 完成日期摘 要通过分析本次箱体一般用于涡轮减速器上，减速器箱体一般采用铸铁砂型铸坯成型，铸铁的抗拉强度、塑性和韧性要比碳钢低。虽然铸铁的机械性能不如钢，但由于石墨的存在，却赋予铸铁许多为钢所不及的性能。如良好的耐磨性、高消振性、低缺口敏感性以及优良的切削加工性能。此外 ，铸铁的碳含量高，其成分接近于共晶成分，因此铸铁的熔点低，约为1200℃左右，铁水流动性好，由于石墨结晶时体积膨胀，所以传送收缩率小在经过机械加工将其加工至使用要求，在生产过程中，减速器箱体的加工工艺定制非常重要，工艺的编制决定了减速器箱体的精度及生产效率，尤其是这种大批量生产的减速器箱体，其工艺规程要考虑到产量问题。同时为了保证工件的加工精度，以及为了提高生产率而研发出各个工序的专用夹具，是操作者使用起来简单、快速、准确，从而在保证精度的前提下大大提高生产率。本文首先介绍了夹具的研究背景和被加工零件的材料、作用和一些特殊工序进行认真的分析，通过对参考文献进行对工时的计算，最后为了方便加工，以及保证加工精度，设计了镗φ100和φ60孔的夹具。关键词：工艺编制，加工时间，专用夹具，生产率全套图纸，加AbstractThrough the analysis on the box are used for turbine reducer, gear reducer box body is made of cast iron sand mold casting forming, commonly cast iron than the tensile strength, plasticity and toughness of low carbon steel. Although the mechanical properties of cast iron is better than steel, but because of the existence of graphite is given by the many cast iron to steel is less than the performance. Such as good wear resistance, high damping resistance, low notch sensitivity, and good machinability. In addition, the carbon content of cast iron is high, its composition is close to the eutectic composition, thus the low melting point of cast iron, which is about 1200 ℃ or so, good hot metal flow, because the graphite crystal volume expansion, so send little shrinkage after machining to its processing to use requirement, in the process of production, the processing technology of the gear reducer box is very important to custom, design process of determines the precision of the gear reducer box and the production efficiency, especially in the mass production of reducer casing, the technical process to production into consideration. At the same time, in order to ensure the workpiece machining accuracy, and in order to improve the productivity and the development of each process of special fixture, the operator is to use a simple, rapid and accurate, and on the premise of guarantee accuracy greatly improved productivity. This art