nanostructured li3v2(po4)3c composite as high-rate and long-life cathode material for lithium ion batteries：纳米结构的li3v2（po4）3c复合率高、长寿命锂离子电池正极材料.pdfVIP

Electrochimica Acta 143 (2014) 297–304 Contents lists available at ScienceDirect Electrochimica Acta j o u r na l h o me p a ge : w w w. elsev /locate/electact a Nanostructured Li V (PO ) /C composite as high-rate and long-life 3 2 4 3 cathode material for lithium ion batteries Senlin Wang a , Zhengxi Zhang a,∗ , Aniruddha Deb b , Chunchen Yang c , Li Yang a,d,∗ , Shin-ichi Hirano d a School of Chemistry and Chemical Engineering, Shanghai Jiao Tong University, Shanghai 200240, PR China b Department of Chemistry, University of Michigan, Ann Arbor, Michigan 48109, USA c Department of Chemical Engineering, Ming Chi University of Technology, Taipei 24301, Taiwan d Hirano Institute for Materials Innovation, Shanghai Jiao Tong University, Shanghai 200240, PR China a r t i c l e i n f o a b s t r a c t Article history: Nanostructured Li V (PO ) /C composite has been synthesized by a facile microemulsion method. X-ray 3 2 4 3 Received 22 May 2014 diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spectra, scanning electron microscopy Received in revised form 7 July 2014 (SEM) and transmission electron microscopy (TEM) results confirm that the as-prepared Li V (PO ) /C 3 2 4 3 Accepted 25 July 2014 sample shows the pure monoc