2016新编存在裂纹的压力容器疲劳断裂分析.docVIP

存在裂纹的压力容器疲劳断裂分析 摘要：为了分析工程中常见的破坏性极大的压力容器疲劳问题，基于断裂力学理论将存在初始裂纹的压力容器等效为无穷远处作用均匀拉应力的含中心裂纹无限大板问题，解出表面半椭圆裂纹和穿透裂纹的应力强度因子；利用断裂判据得到裂纹的临界断裂尺寸；采用Paris表达式对裂纹扩展速率进行描述，推导出初始裂纹在不同裂纹尺寸和形式下的裂纹疲劳扩展寿命。结果表明，对于存在不同尺寸和形式裂纹的压力容器，其疲劳寿命可以由裂纹疲劳扩展寿命明确表示，并且为现役压力容器的安全评定提供一定的理论依据。 关键词：压力容器；裂纹扩展；临界裂纹尺寸；疲劳寿命 Fatigue Fracture Analysis of Pressure Vessel with Cracks Abstract：In order tO study the fatigue of pressure vessel commonly encountered problem in engineering with large destructibility，based on the theory of fracture mechanics，the pressure vessel existing original crack was equivalent tO the problem of infinite flat with center crack．The stress intensity factors of infinite flat forced uniform tensile stress at infinite place with surface half ellipse crack and through crack were deduced．The critical crack size can be ascertained by the criterion．Using the Paris expression tO analyze the crack extends speed，the crack fatigue extension life of different original crack sizes and forms was deduced． The results show that the fatigue life of pressure vessel with different original crack sizes and forms can be clearly expressed by crack fatigue extension life． These analyzed conclusions provide theoretical reference for the active security assess of using pressure vesse1． Key words：pressure vessel；crack extension；critical crack size；fatigue life 1 断裂判据及应力强度因子 由断裂力学理论可知：对于脆性材料．当裂纹尖端的应力强度因子达到该种材料的断裂韧度时，裂纹就会出现失稳扩展而导致结构的破坏。其相应的断裂判据为: ≤ (1) 对于如图1所示的压力容器，在内压力的作用下，将产生轴向正应力和环向正应力。由材料力学方法可知：，. 图1 薄壁圆筒压力容器 由于裂纹的尺寸远小于结构的曲率半径，可以将上述问题等效为无穷远处作用均匀拉应力和的含中心裂纹无限大板问题。 1．1 半椭圆表面裂纹 如图2所示，对于无限大板上的自由裂纹，裂纹边缘任意点处的应力强度因子为： （2） 式中：为前自由表面增大因子，，为后自由表面增大因子，,为塑性区增大困子，，为第2类椭圆积分， 见表1。 图2 半椭圆表面裂纹 表1 第2类椭圆积分 在处，裂纹最深，，且在该点处也最大，是裂纹发展的根源。将代入式(2)得 （3） 对于浅裂纹问题，时，可取，此时椭圆裂纹短轴端点的最大应力强度因子可依式(4)、(5)计算 （4） 当时，对应的临界裂纹尺寸为 （5） 1．2 穿透裂纹 对于存在穿透裂纹的压力容器，将其等