Bi2WO6催化剂的熔盐法合成 毕业论文.docVIP

共 32 页 第 PAGE 33 页 Bi2WO6光催化剂的熔盐法合成 摘 要半导体光催化技术因其在环境净化和能源再生方面的潜在应用而备受关注。新型光催化材料Bi2WO6是最简单的铋层状结构氧化物之一，具有WO6和Bi2O2组成的类钙钛矿片层结构，其禁带宽度相对于TiO2的禁带宽度(3.2 eV)较窄，能被紫外和可见光激发，可同时利用太阳光中的紫外光和可见光，越来越受到广大研究者的青睐。本文以分别以实验室常见的Bi(NO3)3和Na2WO4为原料，以KNO3和NaNO3为熔盐，采用熔盐法在较低温度合成Bi2WO6陶瓷粉体。探讨了合成温度以及反应时间对Bi2WO6粉体的物相结构、形貌以及光催化性能的影响。研究结果表明，500 oC下保温1 h可获得纯相Bi2WO6粉体，其可见光降解罗丹明B的效率可达40 %(2 h)。关键词：Bi2WO6；熔盐法；粉体；光催化性能Molten salt synthesis of Bi2WO6 photocatalystAbstractSemiconductor-based photocatalysis has attracted considerable attentions due to its potential application in the fields of environmental cleaning and energy regeneration. Bi2WO6 is one of the simplest bismuth-layer structural oxides with the perovskite-like slab of WO6 and Bi2O2. Bi2WO6 has a narrower band gap than that of TiO2 and can be excited by both UV and visible light, which made Bi2WO6 attractive for researcher in using solar energy.In the thesis, Bi2WO6 powders were prepared by molten salt method using commercial Bi(NO3)3 and Na2WO4 as raw materials and KNO3/NaNO3 as molten salt, respectively. The effects of synthesis temperature and time on the phases, morphology and photo catalysis properties have investigated. The results indicated that pure Bi2WO6 powders could be synthesized at 500 oC for 1 h and the visible-light-induced degradation efficiency of rhodamine B were 40 % for 2 h.Key words：Bi2WO6; Molten salt method; Powders; Photocatalytic properties绪 论目前，人类社会的可持续发展日益面临着能源匮乏和环境恶化这两大问题，工业的高速发展使得能源和环境问题越来越严重。而正处于工业化和城镇化高速发展阶段的中国，对高效利用太阳能清洁能源及环境保护的技术研发更为紧迫。理论上，从自然界中获取廉价且可持续利用的太阳能，降低制取氢能源成本和分解各种有机污染物是解决上述问题的一个可靠途径。太阳能由于其储存量大、安全性高、能耗低、对环境友好、成本低廉及其独有的地理优越性，使得其在改变能源结构解决能源危机和治理环境污染保护环境的应用方面前景良好。据统计：地球上每年的能量需求为1.09×1020 J，太阳每年向地球辐照约5.4×1024 J的能量，足以提供人们所需的能量。因此研究太阳能能源的潜在价值极大，开发使用太阳能则具有可观的经济效益。因此，利用光催化技术氧化分解有机污染物、分解水制氢在治理污染保护环境、开发新能源改变能源结构方面具有深远的意义。近些年来，一些具有可见光响应的新型钨酸盐光催化材料陆续被研究者们发现。钨酸盐等半导体材料，因其特有的结构和物理化学性质，使