碱性钢包渣对MgO-C耐火的酸腐蚀造成了物质中含量的影响毕业论文外文翻译.docxVIP

熔渣对镁碳耐火材料的腐蚀增加碳含量的影响学校：辽宁科技大学高职学院专业：无机非金属材料工程技术THE INFLUENCE OF CARBON CONTENT ON THECORROSION OF MGO-C REFRACTORY MATERIALCAUSED BY ACID AND ALKALINE LADLE SLAGThis paper describes an investigation of the influence of increasing carbon content on thecorrosion of MgO-C refractorymaterial by molten slag. The refractory material contained massfraction of 98 % MgO, approximately 2 % Fe2O3, and gradedquantities from 3 % to 18 % C. Thecorrosion was investigated in melts of reduction ladle slags at a temperature of 1600 °C inlaboratory conditions. A sample of refractory material with dimensions of 10 × 10 × 100 mm wassubmerged into the moltenslag and exposed to the corrosive effect of the slag for 60 min. Afterthe expose of the refractory material the slag was cooleddown and submitted to a chemical analysis. After a comparison of the MgO content in the slag before and after the corrosiontest the amount of MgO content in the melt was determined and the degree of corrosion of the refractory material wasquantified. The experiments were realised using final slags from the ladle furnace (LF), strongly alkaline slag w(CaO)/w(SiO2) =4.43, and also acidic slags w(CaO)/w(SiO2) = 0.94 with different contents of CaF2. The work was carried out within the frame ofthe projects EUREKA E!3580 and IMPULS FI-IM4/110.RESULTSThe chemical composition of the slags before theexposure is given in the Table 1.Table 1 shows that the acidic slag contains very littleof the CaF2 (w = 0.82 %), and that the alkaline slagcontains 7.18 % CaF2, added to increase its fluidity.Table 1: Chemical composition and alkalinity of the slags used for the corrosion testTabela 1: Kemi~na sestava in bazi~nost `linder, ki sta bili uporabljeni za preizkuse korozijeThe MgO content of the slags after exposure to therefractory material is shown in Tables 2 and 3. Thetables also contain increments of the MgO content andthe increments related to the initial MgO content in theslags (MgO). The six tested samples of refractorym