大掺量矿物掺合料复合水泥浆体的水化产物数量的研究 毕业论文.docVIP

2011年 6月 10日 摘要 本文研究了粉煤灰掺量、硅灰掺量、粉煤灰与硅灰双掺对水泥净浆性能的影响。用XRD定性分析水泥的水化产物，实验结果发现浆体中，Ca(OH)2含量在早期（7d前）增加，后期逐渐减少，并且Ca(OH)2含量随着矿物掺和料掺加量的不同而变化。通过XRD对水泥浆体中的各水化物相进行分析，因而从一定程度上反映了水泥水化反应进程。 同时使用TG-DSC综合热分析方法研究不同掺量，不同养护龄期对复合水泥浆体中水泥水化的影响，其结果与XRD的检测结果相同。 关键词 ：粉煤灰 硅灰 XRD 热分析 Abstract This paper concentrates on the influence of the replacement of fly ash and silica fume and double-mixture of fly ash and silica fume on the performance of cement mortar. The analysis of the hydrated phase of cement is by the means of XRD. And the result is as follows : Ca (OH) 2 content increased at the early stage of hydration (7 days ago)，but decreased after the 7th day. And it changed with replacement percentages of fly ash and silica fume. To some extent, the analysis of the hydrated phase demonstrates the hydrated degree of the cement by using XRD. Meanwhile, in the research, we use TD-DSC to analyze the influence of different replacement percentages of fly ash and silica fume and different curing age on the hydration of cement, the results agree with the results by the means of XRD. Keywords : fly ash silica fume XRD thermal analysis 目录 第一章 概述 1 1.1研究现状与前景 1 1.2 硅灰和粉煤灰性能及其对混凝土耐久性的影响 2 1.2.1 粉煤灰和硅灰性能及应用 2 1.2.2 硅灰和粉煤灰对混凝土耐久性的影响 3 1.3 复合水泥浆体水化产物研究及测定方法 4 1.3.1 测定Ca(OH)2含量的意义 4 1.3.2 测定方法 4 第二章 原材料及试验方案 11 2.1 原材料 11 2.2实验配比方案 11 2.3 实验步骤 12 第三章 XRD对复合水泥浆体的物相分析 13 3.1 引言 13 3.2 试验 13 3.3 试验结果与讨论 14 3.3.1 龄期对水泥水化的影响 14 3.3.2 配比对水泥水化的影响 15 第四章 TG-DSC分析水泥浆体 18 4.1 引言 18 4.2 试验 18 4.3 实验结果与讨论 19 4.3.1 配比对水泥水化的影响 19 4.3.2 龄期对水泥水化的影响 21 第五章 结论与展望 24 5.1 结论 24 5.2 展望 24 致谢 26 参考文献 27 第一章 概述 1.1研究现状与前景 硅酸盐水泥已成为人类最为重要的建筑材料之一，随着国民经济的持续发展，我国水泥年产量逐年增长，在巨大的产量需求及持续不断增长趋势的同时，也伴生了许多问题，如不可再生自然资源与能源的巨大消耗和环境污染等。另一方面，我国水泥熟料的质量与发达国家仍有差距、基础理论缺乏创新、日益的增加工业废渣需要综合利用。 如果通过科学研究，提高水泥熟料的性能，有效地利用数以亿吨计的各类工业废渣，实现节能且具有高性能的水泥生产，那么水泥工业将不仅仅是一个低排废的工业，而且将是一个环保型的工业；水泥将不仅为人类社会提供居住场所，而且将为人类清洁生存环境。 粉煤灰、硅灰都是工业废渣，现在由于逐渐被利用起来，工业废渣的资源化已充分体现，并成为制备高性能混凝土必不可少的活性矿物掺合料组分。许多像粉煤灰、硅灰这样的工业废渣可以在建筑领域中得