影响水电站钢结构焊接变形因素与质量控制 　　摘要：水电站钢结构质量的好坏和焊接施工密切相关，然而焊接变形却影响了水电站整体工程的质量，因此一定要做好焊接变形的质量控制。本文介绍了水电站钢结构焊接变形的种类及其影响因素，从焊前控制、焊接中施工技术、焊后热处理三方面提出了控制焊接变形的措施，为焊工施工提供操作依据，提高钢筋焊接水平，确保钢筋焊接质量。 　　关键词：水电站；钢结构；焊接变形；质量控制 　　Abstract: hydropower station steel structure the stand or fall of quality and welding construction, however, closely related to the welding deformation is affects the whole hydropower station engineering quality, so must do the quality control of welding deformation. This paper introduces the hydropower station steel structure types of welding deformation and its influencing factors, from before welding, welding control in construction technology, postweld heat treatment three aspects put forward control welding distortion measures, for welding construction to provide the basis for operation, improve the steel welding level, ensure that steel welding quality. 　　Keywords: hydropower station; Steel structure; Welding distortion; Quality control 　　中图分类号： TV73 文献标识码：A 文章编号：2095-2104（2013） 　　 　　 　　前言 　　焊接变形是焊件在焊接过程中产生的变形，是钢结构制造中所遇到的一个普遍问题。如何控制好焊接变形是钢结构产品制造成功与否的关键之一，也是难点之一。钢结构是水电站建设中一种重要的建筑结构，焊接是钢结构制安项目的必要施工环节。目前，我国水电建设突飞猛进，机组发电容量增大，钢管直径越来越大，钢结构在其建设项目中的比重大副度增加，管线压力越来越高，因此，发生焊接变形的几率增大。要实现焊接变形的控制，提高水电站建设质量，就必须对钢结构焊接变形的影响因素十分了解，并在此基础上，做好钢结构变形的预防工作。 　　一、焊接变形及其种类 　　焊接变形是指在焊接应力作用下，如果焊件的约束较小，则焊件会产生相应的尺寸变化或弯曲或翘曲变形。 　　焊接变形的种类很多，与构件形状和尺寸，焊接方法和顺序，约束情况等很多因素有关。常见焊接变形主要分为： 　　结构整体焊接变形：①横向收缩变形：②纵向收缩变形：③弯曲变形：④扭曲变形： 　　结构局部变形：①角变形：②波浪变形 　　二、影响钢结构焊接变形的因素 　　（一）材料的热物理性能 　　不同的材料，导热系数、比热和膨胀系数等均不同，产生的热变形也不同，焊接变形也不相同。 　　（二）结构刚性 　　焊后焊缝一般都产生纵向和横向收缩，这种收缩受到整个结构的限制而产生“收缩力”。对于刚性大的焊接结构在这种力的作用下产生的变形比较小；而刚性小的焊接结构在这种力的作用下就产生较大的变形。 　　（三）装配和焊接顺序 　　结构的整体刚性总是比它的部件的刚性大，抗变形能力也大。有了合理的装配顺序还需要有合理的焊接顺序配合，以控制变形。 　　（四）焊接工艺方法 　　不同的焊接方法，将产生不同的温度场，形成的热变形也不相同。一般来说，自动焊比手动焊热集中，受热区窄，变形较小。CO2气体保护焊焊丝细，电流密度大，加热集中，变形小。 　　（五）焊接参数。即焊接电流、电弧电压和焊接速度。线能量愈大，焊接变形愈大。焊接变形随焊接电流和电弧电压的增大而增大，随焊接速度增大而减小。在3个参数中，电弧电压的作用明显，因此低电压、高速、大电流密度的自动焊变形较小。 　　（六）焊缝数量和断面大小 　　焊缝数量愈多，断面尺寸愈大，焊接变形愈大。焊缝若沿构件截面分布不对称，则会引起该构件焊接时产生弯曲变形。 　　（七）焊接