1 - 澳大利亚新型进口矿粉 烧结性能实验研究 摘要 1 - 摘 要 近年我国钢铁产量的大幅度增长，对铁矿石的需求量迅猛增加，但是，铁矿石价格连续大幅上涨，带来高昂的烧结矿成本和铁水成本。钢厂烧结投产以来，烧结矿产量及成本压力一直较大。本文结合钢厂烧结现有的原料条件，在实验室进行了利用澳大利亚进口的新型铁矿粉A矿粉烧结杯试验，烧结杯试验结果表明： （1）A矿粉满足钢厂烧结厂目前在碱度R=2.0、MgO≥2.5%条件下的烧结生产要求，烧结过程中加入一定量的A矿粉可以在一定程度上改善烧结矿的综合性能指标。 （2）烧结过程中配加5%~15%的A矿粉时烧结矿的冶金性能指标可以保持在较为理想的水平； （3）烧结过程配加A矿粉后烧结矿的显微结构发生变化，矿相中还原性能优良的铁酸钙比例增加。 关键词：烧结杯试验；显微结构；冶金性能 ABSTRACT ABSTRACT In recent years, with the growth of Chinas steel production, substantial growth in demand for iron ore increased rapidly, but the continued sharp rise in iron ore prices, resulted in high costs of the sintering and the molten iron ore. Since QingGang sintering plant put into production, output and cost pressures have been significant. In this paper, the laboratory test of A iron ore as one of iron ore fines was conducted in the sinter pot on the conditions of the existing raw materials in QingGang. Experimental results show that : （1）A mineral powder meet production requirements of Qingdao steel plant when it is under the conditions of R=2.0、MgO≥2.5% ，adding some A mineral powder can help improve the sinter comprehensive Eex to a certain extent in sinter process. （2）The sinter performance Eex can maintain a ideal level when 5%~15% A mineral powder were added to in process. （3）The microstructure of sinter mixture changed and the calcium ferrite which have excellent reduction property increased in the proportion when A mineral powder were added to . Keywords: Sinter pot test； Microstructure；Metallurgy performance 目录 目 录 TOC \o 1-3 \h \z \u HYPERLINK \l _Toc 摘 要 PAGEREF _Toc \h I HYPERLINK \l _Toc ABSTRACT PAGEREF _Toc \h II HYPERLINK \l _Toc 1 文献综述 PAGEREF _Toc \h - 1 - HYPERLINK \l _Toc 1.1 铁矿石资源的现状 PAGEREF _Toc \h - 1 - HYPERLINK \l _Toc 1.1.1国内铁矿石资源现状 PAGEREF _Toc \h - 1 - HYPERLINK \l _Toc 1.