无铅硅磷黄铜组织性能研究.docVIP

无铅硅磷黄铜组织性能研究 　　摘要： 采用熔铸法获得65Cu-3Si-0.1P和65Cu-1Si-0.1P两种新型无铅黄铜，利用金相显微镜（OM）、扫描电子显微镜（SEM）、X射线衍射仪（XRD）对其进行物相分析，通过腐蚀试验、拉伸试验、切削试验评价其综合性能.结果表明同时加入Si、P元素后合金中产生大量细小硬质点，可以起到类似铅黄铜中铅质点的作用，从而改善切削加工性能；Si和P的加入亦可大大提高黄铜的耐腐蚀性能. 　　关键词： 　　无铅黄铜； 硅磷黄铜； 金相组织； 切削性能 　　中图分类号： 　　TG 113.25 　　文献标志码： A 　　Research on Microstructures and Properties of 　　Leadfree Silicon Phosphorus Brass 　　XU Yue1， LIU Ping1，2， LIU Xinkuan2， CHEN Xiaohong2 　　（1.School of Mechanical Engineering， University of Shanghai for Science and Technology， 　　Shanghai 200093， China； 2.School of Materias Science and Engineering， University of 　　Shanghai for Science and Technology， Shanghai 200093， China） 　　Abstract： 　　65Cu3Si0.1P and 65Cu1Si0.1P leadfree brass were obtained through casting method.The microstructures of new alloys were analyzed by OM，SEM，XRD，and the comprehensive properties were evaluated through the tensile test，corrosion test and cutting test.The results show that many hard spots were generated as a result of the addition of Si and P，and these hard spots improved the machining performance as the lead particles do in the ordinary brass.The anticorrosion performance can also be significantly improved under the same condition. 　　Keywords： 　　leadfree brass； silicon phosphorus brass； metallographic structure； machining performance 　　0引言 　　普通铅黄铜以其优异的切削加工性能和抗腐蚀性能使其在现代工业中取得广泛应用.但铅黄铜在使用中会产生铅溶出现象而对人体健康造成较大的威胁.所以开发无铅易切削铜合金代替铅黄铜成为各国研究的重要课题[1].在选用替代元素时，要考虑这种元素是否在理论上对切削性能有利，这包括该元素能否与铜形成共晶组织、是否固溶于铜和是否与铜形成化合物[2]；另一方面要考虑在保证切削性能的同时，是否会降低合金的耐腐蚀性能、力学性能等；另外还必须考虑成本因素和环保因素.在满足以上各要求的元素中，Yasuhiro[3]在研究中发现磷和硅对黄铜合金的切削性能较为有利，开发了质量分数为Cu76%、Si3.0%、P0.1%、Zn为余量的硅磷系环保铜合金.但其铜含量相对较高，不利于降低成本.本文在其基础上降低Cu的含量，并进一步降低Si含量，研究其组织与性能.为开发可以推广应用的低铜无铅硅黄铜提供依据. 　　1试验 　　采用熔铸法制备不同成分的铸锭，对其铸态组织、性能进行分析.为起到对比作用，成分设计见表1. 　　从4个铸锭中线切割获取试样，进行研磨、抛光、腐蚀（腐蚀液FeCl3，HCl，腐蚀时间10 s）.在金相显微镜下进行组织观察.在SEM及EDS上进行能谱分析.在显微硬度仪上测试硬度，设置试验力0.98 N，保荷时间15 s.根据国标GB/T 228.1―2010《金属材料拉伸试验第1部分室温试验办法》，在Zwick拉伸试验机上进行拉伸试验，拉伸速率2 mm/min.根据国标GB/T10119―2008《黄铜耐脱锌腐蚀性能的测定》进行腐蚀实验.在C6