中频低损耗功率铁氧体材料 TP4、TP4A TP4S Middle frequency, low core loss power ferrite material TP4、TP4A TP4S;特点： Features： TP4系列材料是一类典型的低损耗材料，主要应用于中频段（～300kHz)。 TP4 series material ,a series of typical low core loss material, mostly are used at middle frequency (～300 kHz).; 具有很低的磁芯损耗和很高的饱和磁感应强度（25℃时大于500mT,100℃时 大于390mT） The core loss is very low and the saturation flux density is very high. (more than 500mT at 25℃, more than 390mT at 100℃); TP4和TP4A磁芯损耗的最低温度点约在90℃，TP4S可用于更高的温度，其磁芯损耗的温度最低点在100~110℃. The temperature of the lowest core loss of TP4 and TP4A is on about 90℃,TP4S can be used within higher temperature band and the temperature of the lowest core loss of TP4S is on 100~110℃. ;应用： Application： 功率变压器 Power transformer 功率电感 Power inductance ;基本特性： Typical Characteristics：;主要特性图: Main characteristics table:;TP4功率损耗特性 Core loss of TP4;;;;TP4;;特点： Features： 低损耗 Low core loss 高饱和磁感应强度 High saturation flux density; 应用温度较低（TP4C：40到45℃； TP4B：60到80℃）应用频率为中频段 （～300kHz） Used on lower temperature （TP4B: 40 to 50℃；TP4C：60 to 80℃) and Middle Frequency （～ 300kHz）;应用： Application： ;基本特性： Typical characteristics:;主要特性图表: Main characteristics table:;;;;高频低损耗功率铁氧体材料 TP5 TP5A Higher frequency, low core loss power ferrite material TP5 TP5A;特点： Features： TP5系列材料是一类可应用于较高频率的 低损耗材料，其应用频率比TP4系列高 （300kHz～1MHz）。 TP5 series material is a series of low core loss material which can be used in higher frequency than TP4 series. (300kHz～1MHz).; TP5A比TP5具有更低的磁芯损耗，尤 其是在1MHz附近。 The core loss of TP5A is the lower than TP5, especially near 1MHz. ;应用: Application： 高频开关电源变压器 Transformer for High Frequency Power Supply 功率电感 Power Inductance DC－DC转换变压器 The Transformer of DC－DC ;基本特性： Typical Characteristics：;主要特性图表: Main characteristics table:;;;;高迭加、高磁导率铁氧体材料 TD5A TD3 High DC bias, high initial permeability ferrite material TD5A TD3;特点： Features： TD系列材料是一类可应用于对迭加要 求较高场合的材料。