石灰改良黄土状硫酸盐渍土强度影响因素研究.docVIP

石灰改良黄土状硫酸盐渍土强度影响因素研究 　　作者简介：文桃（1986），男，四川泸州人，工学博士研究生，Email：wtrm722@126.com。 　　摘要：为充分了解石灰改良黄土状硫酸盐渍土强度的影响因素及规律，对大量不同制备条件的石灰改良黄土状硫酸盐渍土试样进行了无侧限抗压试验和静三轴试验。结果表明：石灰改良黄土状硫酸盐渍土的早期强度较高，但含盐量较高（大于等于1.5%）时，随着养护龄期的增加，其强度并不是一直提高，而是先增大后减小；石灰掺量过多或过少均会使石灰改良黄土状硫酸盐渍土的强度显著降低，灰土比2∶8最接近最佳配灰比；随着土塑性指数的增加，石灰改良黄土状硫酸盐渍土的强度迅速提高；随着含盐量的增加，石灰改良黄土状硫酸盐渍土的浸水强度和不浸水强度都先增大后减小，其峰值强度对应的含盐量约为0.5%；含盐量越高和土塑性指数越大，浸水强度与不浸水强度就越接近；试验结果对石灰改良黄土状硫酸盐渍土地基的工程应用具有参考价值。 　　关键词：黄土状硫酸盐渍土；强度；无侧限抗压试验；静三轴试验 　　中图分类号：TU448文献标志码：A 　　Research on Effect Factors of Strength of Limetreated Loessial 　　Sulfate Salty SoilWEN Tao1， MI Haizhen1， MA Liansheng1，2， WANG Yueli1 　　（1. School of Civil Engineering， Lanzhou University of Technology， Lanzhou 730050， Gansu， China； 　　2. School of Science， Lanzhou University of Technology， Lanzhou 730050， Gansu， China）Abstract： In order to fully investigate the effect factors and influence rules of strength of limetreated loessial sulfate salty soil， a lot of samples of limetreated loessial sulfate salty soil under different conditions were researched by unconfined compression test and static triaxial test. The results indicate that limetreated loessial sulfate salty soil has high early strength. However， when salinity is rather high （not less than 1.5%）， with the increase of curing period， the strength of limetreated loessial sulfate salty soil doesnt increase consistently， but first increases and then decreases. The strength of limetreated loessial sulfate salty soil is reduced significantly when the lime content is too much or too little， and the ratio of lime to soil 2∶8 is closest to optimum mixture ratio. The strength of limetreated loessial sulfate salty soil increases with the rise of plasticity index and first increases and then decreases with the rise of salt content， and the salt content corresponding to peak strength is about 0.5%. The higher the salt content and plasticity index， the closer the strength in water to the strength in air. The experimental results have reference va