等温热处理工艺对Ni5W合金基带立方织构及晶界质量影响.docVIP

等温热处理工艺对Ni5W合金基带立方织构及晶界质量影响 　　摘 要：通过真空感应熔炼方法并采用 RABiTS工艺制备了Ni5W合金基带。通过背散衍射技术（EBSD）对合金基带再结晶热处理后的织构和晶界进行表征。结果表明，Ni5W合金基带在700℃等温处理60min，随后在1100℃等温处理60min后，获得了非常锐利的立方织构，其含量为99.5%（≤10°），小角度晶界的含量也比较高，为98.5%，∑3晶界仅为1.4%。 　　关键词：Ni5W合金基带；热处理；立方织构；晶界 　　中图分类号：TM26+3 文献标志码：A 文章编号：2095-2945（2018）10-0112-03 　　Abstract： The substrate of Ni5W alloy was prepared by vacuum induction melting and RABiTS process. The texture and grain boundary of the alloy after recrystallization heat treatment were characterized by EBSD. The results show that after isothermal treatment at 700℃ for 60 minutes and then isotherm