（毕业论文毕业设计）-Co含量对玻璃光度指标的影响.docVIP

摘要 PAGE IV Co含量对玻璃光度指标的影响 摘 要 熔制玻璃时加入少量玻璃着色剂，可制得各种有色玻璃。玻璃的着色不仅关系到各种颜色玻璃的生产，也是一种研究玻璃结构的手段。对着色玻璃，大家更关注玻璃的色度指标，但对玻璃的光度指标的影响因素相关研究不多。本文通过改变钴玻璃中钴含量、氧化还原剂用量、K2O用量来熔制玻璃样片，同时检验玻璃的热历史，然后用SP—1920 型分光光度计对玻璃样片进行光谱曲线的绘制分析。结果表明：着色剂用量、K2O的添加量及玻璃的热历史均对玻璃光谱曲线有较大影响,配合料的氧化还原气氛对该玻璃的光谱曲线影响不大。 关键词：钴玻璃，熔制，光度指标，光谱曲线 Cobalt content on the influence of glass photometric index ABSTRACT When a small amount of melting glass, glass coloring agents, can be obtained by a variety of colored glass. Colored glass of various colors of glass not only to the production, but also a means of discussing glass structure. Of colored glass, we are more concerned about the color index of glass, but the luminosity of glass studies factors Index few. By changing the cobalt glass cobalt oxide reducing agent, K2O content to melt glass samples, also examined the thermal history of glass, and then use SP-1920 spectrophotometer spectral curves of glass samples for analysis. The results showed that: the amount of coloring agent, K2O of addition and thermal history of glass were on the spectral curve of the glass have a greater impact, with the atmosphere of the redox material spectral curve of the glass has little effect. KEY WORDS: cobalt glass，melting，brightness index，spectral curve 前言 目　录 TOC \o 1-3 \h \z \u HYPERLINK \l _Toc295211042 前　言 PAGEREF _Toc295211042 \h 1 HYPERLINK \l _Toc295211043 第1章 实验 PAGEREF _Toc295211043 \h 2 HYPERLINK \l _Toc295211044 1.1 实验原料及所用设备 PAGEREF _Toc295211044 \h 2 HYPERLINK \l _Toc295211045 1.1.1实验原料 PAGEREF _Toc295211045 \h 2 HYPERLINK \l _Toc295211046 1.1.2所用设备 PAGEREF _Toc295211046 \h 2 HYPERLINK \l _Toc295211047 1.2玻璃的熔制 PAGEREF _Toc295211047 \h 2 HYPERLINK \l _Toc295211048 1.2.1 CoO用量实验 PAGEREF _Toc295211048 \h 2 HYPERLINK \l _Toc295211049 1.2.2 玻璃配合料氧化还原气氛熔制实验 PAGEREF _Toc295211049 \h 3 HYPERLINK \l _Toc295211050 1.2.3 热历史实验 PAGEREF _Toc295211050 \h 3 HYPERLINK \l _Toc295211051 1.2.4 K2O用量实验 PAGEREF _Toc295211051 \h 3 HYPERLINK \l _Toc295211