石屑在混凝土中应用-已经发表.doc

第 PAGE 3 页 共 NUMPAGES 7 页 浅谈石屑在混凝土中的应用 单连梅 刘兴军 张英群 邓承浩 丁建峰 （潍坊万丰混凝土有限公司 潍坊 261041） 【摘要】利用大量的废弃石屑代替部分日益枯竭的河砂，尝试解决砂源的枯竭与建筑业的蓬勃发展的矛盾。首先要保证混凝土的工作性能，其次要保证混凝土的强度指标达到设计要求。唯有如此，才能真正“变废为宝”的实施石屑在混凝土中的广泛应用。 【关键词】石屑、工作性能、强度指标 Discussion on massive concrete of no crack construction in winter Shan Lianmei Liu Xingjun Zhang Yingqun Deng Chenghao Ding Jianfeng (Weifang wangfeng concrete Ltd., Weifang , 261041) Abstract: The use of a large number of abandoned stone chips instead of part of the increasing depletion of river sand, try to resolve the source of the depletion of sand and the construction boom of contradictions. First, the work to ensure the performance of concrete, followed by the strength of concrete indicators to ensure that meet the design requirements. Only in this way can we really turning waste into treasure, the implementation of the chippings in the concrete of the wide range of applications. Key words: Stone chips, work performance, strength index 蓬勃发展的建筑业推动了城市日新月异的变化，伴随而来的是建材的资源的枯竭。在混凝土工业中，砂源的枯竭十分突出；与此同时,采石场中石屑的堆积如山又容易对环境造成粉尘的污染。就潍坊地区而言，石料厂的石屑多数堆积于料厂的边缘。如何利用废弃的石屑替代河砂进行混凝土生产呢？下面对此实施如下的试验。 试验原理 混凝土的生产主要分为两大阶段：第一阶段是混凝土的生产使用过程中要保证混凝土的工作性能——即混凝土的坍落度与和易性，保证能混凝土的可用性：第二阶段是混凝土的主要性能——强度指标，能够达到设计要求。只有这两方面的指标均能满足要求，混凝土才算合格，才能真正的应用于建筑工程中。 试验目的 找出细集料中河砂与石屑的适当比例，生产出合格的商品混凝土，保证混凝土的使用功能和强度指标。 试验原材料 水泥：山东水泥厂 P·O 42.5 表1：水泥主要性能指标 标准稠度用水量（ml） 细度（%） 凝结时间（min） 安定性 强度（Mpa） 初凝 终凝 3天 28天 140 0.8 215 300 合格 24.3 49.9 矿粉：潍坊钢厂S95级矿粉，以上述水泥替代标准水泥 表2：矿粉主要性能指标 强度（Mpa） 掺量50% 活性指数（%） 7天 28天 30.4 49.3 98.8 粉煤灰：潍坊电厂II级煤灰，以上述水泥替代标准水泥 表3：煤灰主要性能指标 细度（%） 强度（Mpa） 掺量30% 活性指数（%） 7天 28天 10 25.2 40.9 83.4 细骨料：石屑+天然河砂 表4 细骨料的主要性能指标 来源 密度（㎏/m3） 泥块含量（%） 含泥量（%） 石粉含量（%） 细度模数 表观 堆积 中砂 2550 1380 0.5 2.8 / 2.8 细砂 2530 1400 0.4 2.2 / 2.3 石屑 2600 1350 / / 8 3.5 表5：石屑的筛分试验结果 筛孔尺寸（㎜） 4.75 2.36 1.18 0.600 0.300 0.150 筛底 分计筛余（%） 1 38 19 20 10 4 8 累计筛余（%） 1 39 58 78 88 92 100 粗骨料：5～31.5碎石 表6：粗骨料（5～31.5㎜碎石）主要性能指标 密度（㎏/m3） 泥块含量（%） 含泥量（%） 针片状含量（%） 压碎指