I I 摘 要 输出波长位于 2μm 附近的掺铥光纤激光器在现代军事技术（光电对抗）、生物 医学和激光雷达等方面都有重要的应用。作为其核心器件的掺铥双包层光纤制备技 术一直被国外研究小组掌握，极大地限制了国内掺铥光纤相关器件的发展。本论文 的目的是研究我们组制备的掺铥双包层光纤的激光性能，为制备出高斜率效率、高 功率的掺铥双包层光纤打基础，打破国外的技术垄断。 本文对已有的双包层掺杂光纤速率方程数学模型进行改进，用龙格-库塔方法对 其进行求解，模拟、分析了铥离子掺杂浓度和光纤长度对掺铥光纤输出激光性能的 影响。 采用改进的化学汽相沉积法（Modified Chemical Vapor Deposition，MCVD）和 汽、液相掺杂技术制备了 6 种掺铥光纤预制棒，用拉丝塔拉制出 6 种双包层掺铥光 纤。 搭建了掺铥双包层光纤激光器系统，对实验室自行制备的 6 种掺铥双包层光纤 优化长度、测试了激光性能（斜率效率、激光波长、阈值）以及弯曲直径和不同泵 浦波长对激光性能的影响，得出以下结论：1.斜率效率最低 27.93%，最高 43.23%， 阈值从 9.2W 到 14.25W 变化，输出激光波长变化范围从 2013nm 至 2043nm；2.使 用掺铥双包层光纤 DCTDF-M004 的激光器，弯曲直径适当变小会增加斜率效率， 当弯曲直径小于一定程度时，会使斜率效率下降；弯曲直径对阈值、输出激光波长 的影响不大；3.掺铥双包层光纤 DCTDF-M006 的最佳泵浦波长位于 791nm 附近， 此时斜率效率最大，为 43.39%；输出激光波长随泵浦波长的增加发生红移；泵浦波 长的变化对于阈值影响不大。对以上测试结果进行分析，为制备出高性能的光纤奠 定基础。 关键词：掺铥光纤 激光性能 斜率效率 激光阈值 弯曲直径 II II ABSTRACT The thulium-doped fiber laser whose output wavelength is 2 micron plays an important role in modern military technology(electrooptical countermeasures),biomed icine and lidar.As the core equipment,the preparation technology of thulium-doped double-cladding fiber has been mastered by foreign research team,which has limited the development of the thulium-fiber-using equipment home.This paper aims to research the laser characteristic of thulium-doped fiber prepared by our team,in order to prepare high slope efficiency and high output power fiber,breaking the monopoly of foreign countries. Firstly,we modify the velocity equation and solve it using the runge-kutta solution.,then simulate and analyse the influence of thulium-ion-doped concentration and fiber length to the laser characteristic. Using the Modified Chemical Vapor Deposition and solution or vapour doping technology,we prepared six kinds thulium-doped perform,then draw them to double-cladding fiber. We establish the thulium-doped fiber laser system and test the laser characteristic(slope efficiency,laser wavelength,threshold) of six thulium-doped double-cladding fiber and the influence of bend diameter and different pump