掺杂Al2O3纳米中空纤维膜的制备及油气渗透特性研究-电气工程专业论文.docxVIP

重庆大学 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV ③ Through the research on temperature oil and the flow rate which influence soil-gas permeation in hollow fiber membrane doped nano Al2O3, it shows that: the range of temperature is restricted in the effect on oil-gas separation capacity in the nano-oxide (Al2O3) hollow fiber membrane; with the increasing of oil flow rate, the gas concentrations of the seven characteristics transformer oil are first increased then stabilized. At the same conditions of temperature and pressure, nano-oxide hollow fiber membrane significantly increases oil-gas permeability characteristics. It lays technical foundation on the improvement of monitoring sensitivity in transformer oil dissolved gas, and great application on on-line monitoring. Key words：dissolved gases, gas permeability, hollow fiber membranes, Al2O3 nano- doping, monitoring sensitivity 重庆大学硕 重庆大学硕士学位论文 目 录 目 录 中文摘要I 英文摘要 II 1 绪 论 1 1.1 变压器油中溶解气体在线监测的研究目的及意义 1 1.1.1 变压器油中溶解气体在线监测技术的研究现状 2 1.1.2 变压器油中溶解气体在线监测装置的研究现状 5 1.2 油气分离是变压器油中溶解气体在线监测的关键技术之一 6 1.2.1 油中溶解气体脱气方法研究现状 6 1.2.2 中空纤维膜在油气分离方面的探索 7 1.3 本文主要研究内容 9 2 提高中空纤维膜渗透特性的机理研究 10 2.1 中空纤维膜研究概述 10 2.1.1 高分子纤维膜的分类 11 2.1.2 中空纤维膜的结构 13 2.1.3 中空纤维膜的评价指标 14 2.1.4 中空纤维膜的制备方法 14 2.1.5 制备条件对膜性能影响研究 16 2.1.6 中空纤维膜的应用进展 17 2.2 中空纤维膜改性研究 18 2.2.1 中空纤维膜改性研究机理 19 2.2.2 中空纤维膜掺杂纳米无机粒子的选择 21 2.3 中空纤维膜油气渗透原理 21 2.4 小结 23 HYPERLINK \l _TOC_250003 3 掺杂 Al2O3 纳米中空纤维膜的制备及渗透特性试验 24 HYPERLINK \l _TOC_250002 3.1 掺杂 Al2O3 纳米中空纤维膜的制备 24 HYPERLINK \l _TOC_250001 3.2 掺杂 Al2O3 纳米中空纤维膜的表征及评价 25 3.3 制膜条件对膜结构及性能的影响 26 HYPERLINK \l _TOC_250000 3.3.1 Al2O3 含量对膜结构及性能的影响 27 3.3.2 干程对膜结构及性能的影响 30 3.3.3 芯液浓度对膜结构的影响 31 3.3.4 凝固浴温度对膜性能的影响 31 3.3.5 卷绕速度对膜性能的影响 32 3.4 试验平台的设计 33 3.5 渗透特性试验 34 3.6 纳米中空纤维膜脱气法与振荡脱气法的对比试验 35 3.7 小结 36 4 渗透特性的对比及原因分析 37 4.1 掺杂 Al2O3 中空纤维膜油气渗透特性分析 37 4.1.1 平衡常数 K 的确定 37 4.1.2 温度特性 37 4.1.3 时间特性 38 4.1.4 渗透率 39 4.1.5 油的流速对渗透效果的影响 39 4.1.6 老化特性 41 4.2 渗透特性对比试验分析 41 4.3 试验结果综合分析 42 4.4 小结 43 5 结论及展望 44 5.1