聚天冬氨酸阻垢机理的研究.docVIP

聚天冬氨酸阻垢机理的研究 　　摘 要：以L-天冬氨酸为原料，H3PO4为催化剂，碳酸丙烯酯为溶剂，微波辐射合成了聚天冬氨酸。静态阻垢法测定PASP具有优良的阻垢性能。运用SEM、IR和XRD对PASP阻碳酸钙垢的结构进行分析。结果表明：加入PASP后，碳酸钙垢形成了新的晶型球霰石，从而起到阻垢作用。 　　关键词：阻垢剂；聚天冬氨酸；阻垢机理；碳酸钙垢 　　中图分类号：TQ423.92文献标识码：A文章编号：1672-1098(2009)01-0023-04 　　收稿日期：2008-01-03 　　作者简介：王剑波(1963-)，男，辽宁丹东人，副教授，博士，研究方向：水处理技术。 　　 　　Study on Antiscaling Mechanism of Polyaspartic Acid 　　WANG Jian-bo1,LU Yuan1,CAO Huai-bao2 　　(1. Department of Chemical Engineering,Anhui University of Science and Technology,Huainan Anhui 232001,China;2. Department of TextileChemistryEngineering, ChangzhouTextileGarment Institute, Changzhou Jiangsu 213000, China) 　　 Abstract:Polyaspartic acid was synthesized by L-aspartic acid as raw material, with H3PO4 as catalyst in medium of propylene carbonate under microwave radition. Its performance of scale inhibition was examined by static scale inhibition testing method, and the results showed that polyaspartic acid is a excellent scale-inhibitor. The structure of calcium carbonate scale inhibited by PASP was investigated by SEM, FTIR and XRD. The results showed that at presence ofPASP, vaterite polymorphs occur in scale, which plays the role of scale-inhibition. 　　Key words:scale inhibitors; polyaspartic acid; antiscaling mechanism; calcium carbonate scale 　　 　　随着“绿色化学”概念的提出，聚天冬氨酸（PASP）作为一种性能优异、可生物降解的绿色化学品日益受到人们的关注，广泛应用于水处理、农业、医药、日用化工等领域［1］。 　　聚天冬氨酸的合成先由原料合成中间体聚琥珀酰亚胺(PSI)，然后PSI水解制取PASP或盐。聚琥珀酰亚胺的合成方法按原料不同分两类：一类是以生化产品L-天冬氨酸(L-ASP)为原料；另一类是使用化工产品C4二元酸，如马来酸酐、马来酸或富马酸作为基本原料。国内外学者采用传统加热方法对PASP的合成工艺进行了系统研究［2-5］。 但传统的加热方法， 反应时间长、 耗能大。课题组以L-天冬氨酸为原料，微波辐射催化合成聚天冬氨酸［6］890-892。在此基础上采用SEM、IR和XRD分析技术对PASP阻CaCO3垢的阻垢机理进行了初步探讨。 　　 　　1 实验 　　 　　1.1 聚天冬氨酸的合成及性能测试 　　参照文献［6］??890-892，以L-天冬氨酸为原料，H3PO4为催化剂，碳酸丙烯酯为溶剂，微波辐射合成聚天冬氨酸。 　　实验参照文献［7］，测定PASP对碳酸钙垢的阻垢率。在去离子水中加入一定浓度的Ca2+、HCO-3和聚天冬氨酸阻垢剂的溶液，在一定温度恒温水浴中放置一段时间后，用EDTA络合滴定法分析测定其上层澄清液中的钙含量，以测定阻垢率，计算公式 　　阻垢率=(C1-C0)/(C2-C0)×100% 　　式中：C1为加PASP水样加热后溶液中Ca2+的浓度，mg/mL；C2为未加PASP不加热时溶液中Ca2+的浓度，mg/mL；C0为未加药剂加热后溶液中Ca2+的浓度，mg/mL。 　　1.2 聚天冬氨酸阻碳酸钙垢机理