将纳米TiO颗分散在硅酸盐上在紫外.docVIP

将纳米级TiO2颗粒分散在硅酸盐上在紫外-可见光下光催化降解染料污染物 Jingyi Lia , Chuncheng Chena , Jincai Zhaoa*, Huaiyong Zhub .Jason Orthmanb 　 Centre for Molecular Science, Institute of Chemistry, The Chinese Academy of Science, Beijing 100080, China Nanomaterials Centre and Department of Chemical Engineering, The University of Queensland, St. Lucia, Qld 4072, Australia 　　Received 30 November 2001; received in revised form 7 January 2002; accepted 9 January 2002 　 Abstract 　　A novel catalyst, TiO 2 nanoparticles dispersed in silicate, were used to photodegrade sulforhodamine B (SRB) under UV–VIS irradiation. With good photocatalytic activity and the ability to be readily separated from the reaction system, this novel catalyst exhibits the potential to be effective in the treatment of dye pollutants in aqueous systems. 2002 Elsevier Science B.V. All rights reserved. Keywords:Titania; Silicate; SRB; UV–VIS irradiation 1、引言 基于藤岛和本田报道了他们致力于研究在水中以TiO2为电极[1]的催化特性，并得出了其催化效率有效增加了，近年来在异构环境复原与光催化剂的光催化是最活跃的领域之一，TiO2的催化特性已经应用于催化分解废水中的有机物[2,3]。 在TiO2的催化作用并在光触媒—紫外线照射下许多有机污染物都可降解并且矿化[4–12]。 以下是靠氧化光降解有机物并广泛得到认可的结构。一旦TiO2粒子被紫外光辐射h+立刻形成。这里，一些主要来自于依靠光h+氧化OH-或H2O?OH的自由基负责对样品结构的初步破坏。氧的存在也是至关重要的，其主要作用是作为一个高效的e—“捕捉器”生成了O2—从而阻止了e—和h+的重组。氧化有机基质湿度通过这一机制可以发生反应(1): RH 或 R?+{O2, O2? ?, HOO?或OH} →过氧或羟基中间体 →→降解或矿化产品 (1) 然而，有两个问题严重限制这种光催化反应的应用。 第一个限制问题是人造紫外光源价格昂贵，天然紫外光在阳光中只占一小部分 （约3-5 %)。 第二个限制问题是二氧化钛粒子难以从处理后的水中分离出来。 最近，我们报道的在液态分散的二氧化钛并曝露在可见光下可降解多种染料[13–17]。已知的辐射机制依赖其本身结构。(2)–(7)已被证明在紫外线下染料的降解不能实现并且它的实现并不是由于TiO2而是因为可见光的作用 dye + hν→dye? (2) dye?+ TiO2→dye?+TiO2(e ) (3) TiO2(e ) + O2 →TiO2 + O2? ? (4) O2?-+ TiO2 (e ) + 2H+→H2 O2 (5) H2 O2 + TiO2(e ) →?OH+ OH? (6) dye? +O2 (or O2? ? or?OH) →基团或羟基中间体 →→降解或矿化产品 (7)