有关非调质低焊接裂纹敏感性钢WDB620研究开发.pdfVIP

非调质低焊接裂纹敏感性钢WDB620 研究开发 常跃峰 谢良法 姚连登 赵文忠 （舞阳钢铁有限责任公司） 摘要 按照 CF62 钢的技术要求，设计了一种 620MPa 级低焊接裂纹敏感性钢。采用微合金 化结合控轧控冷工艺，免去了淬火工序，以晶粒细化、沉淀强化、位错强化和贝氏体组织强 化为主要手段，辅以回火处理获得了成功,并对钢的可焊性进行了评价。产品已应用于水电 站压力钢管系统及 108 吨电动轮自卸车。 关键词 非调质 低焊接裂纹敏感性 开发 Research and Development of Non Quenched and Tempered Low Welding Crack Susceptibility Steel WDB620 Changyuefeng Xieliangfa Yaoliandeng Zhaowenzhong (Wuyang Iron Steel Co.Ltd) Abstract A kind of 620MPa low welding crack susceptibility steel was designed according to the technical requirements of CF62.It meets with success by adopting microalloying combined with controlled rolling and controlled cooling process,exempting quenching sequence,taking main means of grain refining,precipitation strengthening ,dislocation strengthening and bainite structure strengthening as well as the supplementary means of tempering treatment,also makes assessment to the weldability of the steel.The product has been used for pressure steel pipe system of hydropower station and 108t self-discharging truck with electric operated wheel. Keywords non quenched and tempered,low welding crack susceptibility,development 1 前 言 为了满足大型钢结构对低焊接裂纹敏感性钢的需求，自 20 世纪 70 年代，国 际上开始研制 CF 钢——低焊接裂纹敏感性钢（国外也称焊接无裂纹钢）。由于 当时在世界范围内对控轧工艺的研究还处于起步阶段，因此，当时在开发抗拉强 度 60Kg 级 CF62 钢只能采用淬火+ 回火手段。WDB620 的开发目的是替代大量进 口的 CF62，它是在传统淬火型 CF 钢基础上，采用非调质技术发展起来的新一 1 代低焊接裂纹敏感性钢，非调质钢的发展是微合金化技术和热机械处理及其冷却 技术发展的结晶, 非调质钢产量和品种的多样性是钢铁强国的标志[1] 。当今 TMCP、TPCP 工艺的不断涌现，使省去传统淬火工序生产屈服强度 460MPa 级 别以上低合金高强度钢的梦想变成了现实，这一工艺技术经过不断发展和完善， 现在代表着国际低合金高强度钢发展的最新成果和发展方向。国外已大量用于桥 梁、高层建筑、工程机械、管线、军用舰船，并正在向压力容器等领域推进。 WDB620 钢按低碳贝氏体钢设计，其优良性能主要来自钢的组织细化以及 贝氏体中的高密度位错。WDB620 采用控轧工艺，免去了淬火环节，节约了工序、 节约了能源、保障了优良板型，钢的强化主要依靠微合金元素的沉淀强化、细晶 强化、位错强化及组织强化