基于微观结构量化的SBS改性沥青分析 杨 群，殷 巍 （同济大学 道路与交通工程教育部重点实验室, 上海200092） 摘 要：针对SBS（苯乙烯-丁二烯-苯乙烯嵌段共聚物）改性沥青显微结构的量化研究方法，以SBS改性沥青偏光400倍显微结构图为研究对象，在已有量化分析方法的基础上，提出一种定量评价SBS改性沥青微观结构新方法。结果表明：新方法操作相对简单，可从微观角度量化分析不同改性剂对SBS改性沥青性能影响，结论与实验结果一致。 关键词：SBS改性沥青；改性剂类型；微观结构；定量分析 中图分类号：U 491.2；U 492.8 文献标识码：A Novel performance measurements of SBS modified asphalt based on microstructure pictures Yang qun Yin wei (Key Laboratory of Road and Traffic Engineering of the Ministry of Education, Tongji University, Shanghai 201804, China) Abstract: The objective of this paper is to establish novel quantitative performance measurements for SBS (styrene-butadiene-styrene block copolymer) modified asphalt based on microstructure pictures of asphalt specimens. By magnifying pictures 400 times via microscope, two new measurements including area ratio of modifier and homogeneity of modifier distribution were tested for asphalt specimens with three vary modifier. Then the relationship between two new measurements and traditional measurements including penetration number, ductility rotational and viscosity rotary were investigated. The results indicated that they have a good correlation. It was concluded that quantitative measurements through microstructure pictures are a reliable and relatively easy method to evaluate performance of asphalt. Key words: SBS modified asphalt,;type of modifier;microstructure;quantitatively analysis 随着改性沥青在公路建设中的广泛应用， SBS（苯乙烯-丁二烯-苯乙烯嵌段共聚物）改性沥青凭借着优异的性能在我国公路建设中发挥了重要的作用。研究表明， SBS改性沥青的微观结构与其性能有着密切的联系[1]，微观结构的差异对其性能起到极其重要的决定作用[2]。 国内外对SBS改性沥青微观结构研究从初步定性化评价聚合物对沥青的改性效果到运用专业软件对改性剂微粒大小、形态进行分析。现阶段运用专业软件处理分析方法为：在运用荧光显微镜观测到SBS改性剂在沥青相中的真实形态的基础上，配备数字化处理所需的硬件设备及功能完善的图像处理软件对SBS改性沥青微观结构图像进行分割、记数、测量[4]。此方法由于专业软件的操作复杂，对实验硬件要求较高，对于普通的偏光显微镜所成图像来说，不满足专业图像处理软件对分析对象的要求。因此，本文提出一种新的技术方法，打破专业软件的应用限制，运用基础操作软件对SBS改性沥青微观结构进行较深层次的量化研究，从而指导实际生产实践。 1 试验研究 1.1 试验材料 （1）基质沥青 本文选用的基质沥青为东海AH-70号沥青，其基本技术参数如表1所示。 表1基质沥青基本技术参数 Table1 Basic technical parameters of matrix asphalt 检测项目 检测结果 软化点/℃ 55 针入度(100