针对陶板幕墙模拟地震振动台试验研究.PDFVIP

陶板幕墙模拟地震振动台试验研究 黄小坤，林祥 （中国建筑科学研究院北京 100013） 黄拥军 （北京江河幕墙装饰工程有限公司 北京 101301） [摘 要] 通过钢结构框架外挂足尺陶板幕墙模型的震动台试验，研究了陶板幕墙的抗震性能。试验分别 输入 El centro 地震波、人工波及 Taft 记录波。试验结果表明，所测试的陶板幕墙系统具有良好的抗震性能， 符合抗震设计要求。 [关键词] 陶板幕墙 振动台试验 抗震性能 Study on Ceramic Curtain Wall by Shaking Table Test Huang Xiao-kun, Lin xiang, Liao Yu-biao (China Academy of Building Research, Beijing 100013) Huang Yong-jun (Beijing Jianghe Curtain Wall Decoration Engineering Co.Ltd, Beijing 101301) [Abstract] In order to testify and study the seismic behavior of ceramic curtain wall, a steel frame model with full-scale ceramic curtain wall system was made and the shaking table test was done. El Centro wave, man-made wave and Taft wave were selected to input respectively in the test. The results show that the inspected ceramic plate curtain wall system behaves quite well and the seismic design requirements are met. [Keyword] ceramic plate curtain wall; shaking table test; seismic behavior 1 概述 幕墙系统自身承受的地震作用通常较小，但地震作用具有动力特性，对连接节点影响较 大，而连接节点的破坏有可能导致幕墙的损坏或脱落。模拟地震振动台模型试验是目前研究 幕墙地震反应和破坏机理的最直接、最有效的方法之一。 陶板幕墙系统在国内应用较少，尚缺乏地震区的工程实践经验；同时，我国有关现行幕 墙规范尚无相关的内容及规定。本文结合北京江河幕墙装饰工程有限公司在北京完成的一个 陶板幕墙工程（南新仓商务大厦），进行了陶板幕墙的抗震性能试验检验和研究，检验其抗 震性能是否符合设计要求。实际工程位于北京市，抗震设防烈度为 8 度，设计基本地震加速 度为 0.2g，场地为Ⅱ类。 试验模型的主体支承结构采用钢框架，外挂陶板通过幕墙的横梁、立柱及连接件与钢框 架连接。试验在北京工业大学的 3m ×3m 振动台上进行，模型照片见图 1。本次试验的主要 目的是检验该陶板幕墙系统在8 度地震区的抗震性能和安全可靠性。 图 1 试验模型 图 2 幕墙连接节点 1 2 试验方案 模型主体结构采用平面尺寸为 2.464m ×2.680m 的钢框架，其层高为 4.25m ，与实际工 程相同。模型主要受力构件 （柱、梁）采用方钢管和矩形钢管，梁、柱的截面尺寸由结构动 力时程分析计算确定，以保证模拟大震作用下构件基本处于弹性工作阶段，从而保证陶板幕 墙系统抗震性能研究的可信度。梁、柱的连接均为焊接。 在模型框架的结构南、北、西三个立面外挂陶板幕墙，使试验能全面地验证陶板幕墙在 面内 （沿振动方向，即东西向）及面外 （垂直于振动方向，即南北向）的抗震性能。单块陶 板的尺寸为 463mm ×250mm ×15mm ，幕墙与主体结构连接节点见图2 。 陶板本身及其布置方式、连接节点等均与实际工程相同。为便于观察试验现象，在东面 未悬挂陶板幕墙，见图 1。 3 试验设备、测点及地震波 3.1 振动台 振