图78彩印疏水改性核壳结构颗粒对Pickering乳液的稳定作用
[在此处键入]
收稿日期:2018-00-00;定用日期:2018-00-00;DOI:10.13550/j.jxhg.201803190185
基金项目: 国家自然科学基金(217061478)
作者简介: 姜秋艳( 1994-) ,女,硕士研究生。联系人:李秋红( 1979-),女,电话:0533-2782232,E-mail: qhli@
功能材料
功能材料
(图7、8彩印)疏水改性核壳结构颗粒对Pickering乳液的稳定作用 201803190185
姜秋艳,李自闯,李秋红*,李爱香,丛日敏,司维蒙
(山东理工大学 材料科学与工程学院,山东 淄博 255000)
摘要:为了探究固体颗粒对乳液的稳定作用,采用双亲染料分子罗丹明B对核壳结构的Fe3O4@SiO2纳米颗粒进行疏水改性,并将改性后的纳米颗粒作为稳定剂制备Pickering乳液。通过Zeta电位、FTIR、XRD、SEM、接触角测量、光学显微镜、电导率仪对Fe3O4@SiO2纳米颗粒以及Pickering乳液的结构、形貌和性能进行表征与分析,结果表明:制备的纳米颗粒粒径小,约为150 nm,为单分散球形核壳结构;罗丹明B成功修饰到Fe3O4@SiO2纳米颗粒表面,改性后颗粒接触角由30°增加至120°;随乳化剂颗粒质量浓度的增加,制备的乳液液滴的粒径减小。另外,所得Pickering乳液具有良好的磁场响应性,可通过外加磁场实现对乳液稳定性的可逆调控,且此过程可重复3次以上。
关键词:罗丹明-B;疏水改性;Pickering乳液;磁场调控
中图分类号:O647 文献标志码:A 文章编号:
Hydrophobic Modification of Core-shell Nanoparticles and Its Stabilizing
Effect on Pickering Emulsions
JIANG Qiu-yan, LI Zi-chuang, LI Qiu-hong*, LI Ai-xiang, CONG Ri-min, Si Wei-meng
(School of Materials Science and Engineering, Shandong University of Technology, Zibo 255049, Shandong, China)
Abstract: In order to explore the stabilizing effect of solid particles on the emulsions, core-shell Fe3O4@SiO2 nanoparticles were hydrophobically modified by Rhodamine B and then the resulting modified nanoparticles were used as stabilizer to prepare Pickering emulsions. The structure, morphology and properties of modified Fe3O4@SiO2 nanoparticles and Pickering emulsions were characterized and investigated by Zeta potential, FTIR, XRD, SEM, contact angle measurement, optical microscope and conductivity measurement. The results showed that mono-dispersed, spherical and core/shell structure nanoparticles with particle diameter 150 nm were synthesized successfully. Rhodamine B was successfully introduced onto the surface of Fe3O4@SiO2 nanoparticles. After Fe3O4@SiO2 nanoparticles was modified, its contact angle increased from 30° to 120°. The particle size of the emulsion droplets decreased with the increase of emulsifier mass concentration. Moreover, the resulting Pickering em
1亿VIP精品文档
相关文档
最近下载
- 3岁-4岁 《美味的甜甜圈》-美术课件.pptx
- 丰田新能源汽车协同创新研究与启示.docx
- 职业卫生与职业医学教学大纲及教案.pdf
- 鲁德公司柴油车改装LNG CNG天然气资料.ppt
- IGCSE 核心数学 2016年夏季 真题试卷4(含答案)版本2 IGCSE Core Math 2016 Summer Past Exam Paper 4 (with answer) v2.pdf
- 加速康复在普外科的护理实践-省康复护理专科护士培训班课件.pptx
- 储能EMS能量管理系统[汇编].pdf
- “挑战杯大学生创业计划大赛-作品模板_完整.pdf
- 软件源代码编写规范.doc
- 英剧剧本唐顿庄园台词本中英文对照精排版第一季第一集.pdf
文档评论(0)