ZrC粉体制备的研究进展.PDFVIP

ZrC粉体制备的研究进展 赵彦伟摇 摇 刘宏瑞摇 摇 李军平摇 摇 胡继东摇 摇 陈海坤 (航天材料及工艺研究所,先进功能复合材料技术重点实验室,北京摇 100076) 文摇 摘摇 ZrC作为一种先进的高温结构陶瓷材料,在航空航天、清洁能源(第四代核技术)等领域具有广泛 的应用。 本文主要综述了ZrC粉体的制备技术,主要有直接合成法、机械合金化法、自蔓延高温合成法、碳热还 原法、溶胶-凝胶法、液相前驱体法、激光气相反应法和高频等离子体法等,详细分析了各制备技术的特点。 关键词摇 ZrC,制备技术,碳热还原法,溶胶-凝胶法,高频等离子体法 Progress on Preparation of ZrC Powders Zhao Yanwei摇 摇 Liu Hongrui摇 摇 Li Junping摇 摇 Hu Jidong摇 摇 Chen Haikun (Science and Technology on Advanced Functional Composites Laboratory,Aerospace Research Institute of Materials Processing Technology,Beijing摇 100076) Abstract摇 As an advanced high temperature structural ceramics,zirconium carbide iswidely used in aerospace, cleaning energy (the fourth generation nuclear technology) and other related areas.The preparation technology of zir鄄 conium carbide powders is reviewed in detail,including direct reaction,mechanical activation,self鄄propegating high鄄 temperature synthesis,carbothermal reduction,sol鄄gel,liquid precursor,laser pyrolysis,high frequency plasma,among others.The characteristics of the preparation techniques are detailedly analyzed. Key words摇 Zirconiumcarbide,Preparationtechnique,Carbothermal reduction,Sol鄄gel method,Highfrequency plasma 0摇 引言 结助剂,如Ni、LaB 、SiC、MoSi 、Zr和C等[11-14] ,但会 6 2 目前,常用的超高温材料有难熔金属及其合金、 降低材料的高温性能。 无压烧结是制备ZrC材料最 金属间化合物、超高温陶瓷及基体掺杂改性抗氧化 具有实际意义的致密化方法,但是其原料粉末颗粒表 [1-4] 面ZrO 膜的存在导致烧结过程变得复杂,而ZrO 的 C/ C复合材料 。 其中,超高温陶瓷,尤其是难熔 2 2 金属Zr、Hf和Ta 的碳化物和硼化物具有高熔点、高 挥发温度要在2000益以上,此温度下,ZrC粉末的粗 强度、高模量、高硬度、热力学稳定性好、导热性好等 化已经发生,势必会影响材料的致密化和最终性能。 优异性能,是飞行器鼻锥、机翼前