牵伸力应用於异型断面聚酯与棉混纺纱最佳纺纱牵伸条件之探讨.PDFVIP

牽伸力應用於異型斷面聚酯與棉混紡紗最佳紡紗牽伸條件之探討 Optimum Drafting Conditions of the Profiled Polyester and Cotton Blend Yarn with the Application of the Drafting Force 蘇清淵、方俊賢 * 台灣科技大學 高分子工程學系 Fax: (02) 2737-6544 E-mail: M9104208@mail.ntust.edu.tw ABSTRACT 故 本研究針對利用牽伸力應用於探討最佳之紡紗條件， For the optimum drafting conditions of the Profiled 針對混紡聚酯及棉粗紗，進行相關參數的實驗，例如：羅拉 Polyester Fiber (with the function of Moisture Absorption and 隔距、初牽伸比、粗紗重量、混紡的比例等，以探討其與牽 Release) and Cotton fiber blend yarn (P/C yarn) spinning, the 伸力間的關係，並探討粗紗牽伸力及其變異係數與紗品質之 application of the drafting force has to be studied. In this work, 間的相關性，在實驗過程中，尋找對應於最佳紗品質之初牽 we precede the experiment of the drafting force based on the P/C 伸比以期達到高支紗、高品質的目標。 roving to investigate the influence of the roller gauge, draft ratio, and blend ratio on the drafting force. We understand the drafting 三、實驗 force of the P/C roving follow the same trend as for the regular 3.1.實驗材料 T/C roving. However, the character of the drafting force reveals 本實驗所使用遠東紡織股份有限公司提供之異型斷面聚 some difference between them. 酯纖維及天然棉 ，纖維規格如下： Keywords ：Profiled Fiber, Moisture Absorption and Release , (1)原棉 ：細度：4.3(micronair) Draft Force, 長度：28.7(mm) 強度： 3.3(g/d) 一、中文摘要 (2)聚酯 ：細度：1.4(micronair) 本研究係利用牽伸力應用於具有吸濕排汗(Moisture 長度：38(mm) Absorption and Release) 功能之異型斷面聚酯纖維( Profiled 強度： 3.9(g/d) Fiber )與天然棉( Cotton )混紡 紗( P/C Yarn )最佳紡紗牽伸條 斷面：十字型斷面 件之探討。實驗中利用牽伸力測定器，以異型斷面聚酯與棉 (3) 粗紗規格：230gr/30yd 混紡粗紗為原料，進行 P/C 粗紗牽伸力測試。探討其不同之 羅拉隔距、初牽伸、 P/C 混紡比等對牽伸力之影響，以了解 3.2實驗設備 異型斷面聚酯纖維與棉混紡粗紗於牽伸過程中，有別於傳統 (1)改良式牽伸力測定器 （如Figure 2所示） T/C 粗紗的牽伸行為，藉以改善異型斷面聚酯與棉混紡紗之 (2)AMD Athlo