　　　　　　　　　　　　　　　　　阀 　　　门 　　　　　　　　　　　　2001 年第 4 期 —18 — 文章编号 : (2001) 镍系低温用钢缺口韧性的研究 王晓芬 (上海良工阀门厂 , 上海 　200082) 　　摘要 　通过对材料的试验检测及金相与电子断口分析 , 总结出调质工艺、正火 + 调 质及不同的加热与回火温度对 L F3 锻钢和 LC3 铸钢低温韧性的影响 , 为改善这 2 种钢 低温韧性的稳定性提供了良好的方法。 　　关键词 　低温阀 ; 低温钢 ; 冲击韧性 ; 研究 　　中图分类号 : TG156 　　　　文献标识码 : A Study on toughness of steel notch for nickelbase in low temperature WAN G Xiaofen ( Shanghai Liang Gong Valve factory , Shanghai 200082 , China) Abstract : Though testing and inspection of the material and notch analysis of metallography and electronics , the summary is given that different heat treatment such as hardening and tempering process , normalizing plus hardening and tempering , as well as temper tempera ture have influenced on the toughness of low temperature of L F3 forge steel and LC3 cast steel. Provide better methods for improving stability of the toughness of low temperature of the two kinds of steel. Key words : low temperature valve ; low temperature steel ; impact toughness ; studying 1 　概述 时 , 其低温韧性不稳定 , 波动比较大的问题通 L F3 和 LC3 均为低温下使用的 35Ni 钢。 过试验探讨在相同成分下 , 热处理工艺对其低 该钢具有良好的低温韧性 , 广泛用于制造工作 温韧性的影响。 温度为 - 45～101 ℃的石油和化工等行业的低 2 　材料的化学成分和机械性能 温设备。如液化天然气、液化石油气、煤气化 试验材料系 ASTM 标准中的 L F3 牌号锻 和乙烯等工程生产、储存、运输所需的容器、 钢和 LC3 牌号铸钢。其化学成分和实测性能 管道部件及阀门等。本文根据制作低温阀门 指标见表 1 。 表 1 　试验材料的化学成分和机械性能 化学成分　w t/ % 机械性能 材料