溶剂热法制备硫化镍空心微球PreparationofNiSHollow.PDF

2006 年第 64 卷 化 学 学 报 Vol. 64, 2006 第 1 期, 85～88 ACTA CHIMICA SINICA No. 1, 85～88 ·研究简报· 溶剂热法制备硫化镍空心微球 陈广大 a,b 褚海斌 a 李雪梅 a 金 钟 a 李 彦*,a (a 北京大学化学与分子工程学院 北京 100871) (b 上饶师范学院化学系 上饶 334001) 摘要 以醋酸镍和硫代乙酰胺为原料, 乙醇为溶 , 在 150 ℃的溶剂热条件下制备了硫化镍空心微球, 并用 XRD, TEM, SAED 和 SEM 对产物进行了表征. 结果显示, 这些空心微球由 β -NiS 和 α-NiS 组成, 从反应开始得到的 α-NiS 实 心球通过内核的消溶演变而成. 关键词 NiS; 空心微球; 溶剂热 Preparation of NiS Hollow Microspheres by Solvothermal Method CHEN, Guang-Daa,b CHU, Hai-Bina LI, Xue-Meia JIN, Zhonga LI, Yan*,a a ( College of Chemistry and Molecular Engineering, Peking University, Beijing 100871) (b Department of Chemistry, Shangrao Normal College, Shangrao 334001) Abstract NiS hollow microspheres were synthesized by the reaction of nickel acetate and thioacetamide in ethanol at 150 ℃. XRD, TEM, SAED (selected area electron diffraction), and SEM were utilized to charac- terize the products. The results show that the products were hollow microspheres made of β - and α-NiS, while the hollow spheres were transformed from the α-NiS solid ones. Keywords nickel sulfide; hollow microsphere; solvothermal 微米、纳米大小的空心球结构的物质具有密度小、 今为止, 只有 Hu 等[12,13]在 γ 射线照射下, 以 PMMA (聚 比表面积大等优点, 在填充材料、药物传输[1] 、催化[2,3] 甲基丙烯酸甲酯)分解得到的 MMA ( 甲基丙烯酸甲酯) 等领域具有潜在的应用前景, 因而得到了广泛的关注. 油滴为模板制得了 NiS 空心球. 在本文中, 我们以乙醇 例如 Dhas 等[2]用超声化学法制备的二硫化钼纳米空心 为