ZG20SiMn铸钢件热处理工艺.PDFVIP

ZG20SiMn铸钢件热处理工艺 焦何生，尚贺军 (济钢集团重工机械有限公司，山东 济南 250101) 摘要：ZG20SiMn铸钢件空冷正火即可获得一定的表面硬度，但冲击韧性不足。热处理工艺 试验结果表明,采用920℃风冷正火、650℃空冷回火的热处理工艺,可得到较均匀的硬度(约 155HB),其珠光体组织也较为细小、均匀,从而满足工件的力学性能要求。 ZG20SiMn ZG20SiMn 关键词：ZZGG2200SSiiMMnn；热处理工艺；力学性能 TheHeatTreatmentProcessforZG20SiMnCastSteelpart TheHeatTreatmentProcessforZG20SiMnCastSteelpart TThheeHHeeaattTTrreeaattmmeennttPPrroocceessssffoorrZZGG2200SSiiMMnnCCaassttSStteeeellppaarrtt JIAOHesheng SHANG Hejun JIAOHesheng SHANG Hejun JJIIAAOOHHeesshheenngg，SSHHAANNGGHHeejjuunn (HeavyMechanicalEquipment CompanyofJinanIronSteel GroupCo.,Ltd.,Jinan250101) Abstract Abstract AAbbssttrraacctt：ZG20SiMn cast steel part will provide higher surface hardness but insufficient impact toughness after normalizing. The heat treatment process test reveals that relatively uniform hardness(about 155HB) and fine-uniform pearlitic microstructure can be obtained by means of normalizing from 920℃with wind cooling and subsequently tempering at 650℃with air cooling fortheZG20SiMn caststeel,thusmeetingtheneedsofpartinmechanicalproperties. Keywords ZG20SiMn Heattreatment process Mechanicalproperties Keywords ZG20SiMn Heattreatment process Mechanicalproperties KKeeyywwoorrddss：ZZGG2200SSiiMMnn；HHeeaattttrreeaattmmeennttpprroocceessss；MMeecchhaanniiccaallpprrooppeerrttiieess ZG20SiMn铸钢具有良好的铸造性能及焊接性能。一般用作铸造大截面壁厚重型铸件， 如水压力机、工作缸、水轮机转轮、叶片、电站主轴、法兰、坐环等，凡是高韧易焊铸钢件 均可适用。ZG20SiMn 钢铸态组织为珠光体和铁素体，正火后容易出现魏氏组织，当铸件粘 [1] 砂严重时，为了便于清砂，可予先进行一次高温（1100℃）扩散退火 。 ZG20SiMn铸钢正火和回火是为了获得细小和均匀的显微组织以改善钢的强度和韧性， 热处理奥氏体化加热温度范围一般为材料的 A +（40～60）℃。对于含有少量合金元素的 c3 ZG20SiMn 铸钢来说,由于铸造过程造成的合金元素的偏析和碳化物等在奥氏体中溶解不充 分,造成奥氏体成分不均匀，其强韧性能很难得到充分发挥。我们为某公司生产的ZG20SiMn 铸钢工件如图1所示，试生产时的热处理工艺为:工件正火加热保温