含镀锡镍玻璃纤维新型电磁屏蔽涂料的研制-安全与电磁兼容.PDF

MATERIAL A PPLICATION IN EMC 镀锡镍玻璃纤维新型电磁屏蔽涂料的研制 Development of a New Kind of Electromagnetic Shielding Composite Coating Containing Sn-Ni-coated Glass Fibre 1 2 成都理工大学 矿产资源化学四川省高校重点实验室 1 1，2 1 1 1，2 1 雷停 管登高 徐冠立 孙遥 龚赢赢 孙传敏 摘要 以镀锡镍玻璃纤维与镍粉为复合填料，以丙烯酸树脂作为粘结剂，按照涂料制备的方法，研制了一种新 型电磁波屏蔽复合材料- 镀锡镍玻璃纤维/ 镍粉/ 丙烯酸树脂电磁波屏蔽复合材料。测试结果表明，其电磁 屏蔽效能可达 35.082 ～41.924 dB ，并介绍了其主要特点和作用，展望了应用发展的前景。 关键词 电磁环境污染；电磁波屏蔽；屏蔽涂料；屏蔽效能；镀锡镍玻璃纤维 Abstract According to the coating preparation method, a new type of electromagnetic shielding composite material was prepared with Sn-Ni-coated glass fibre and nickel powders as the composite packing and with acrylic resin as binder. The test results showed that its electromagnetic shielding effectiveness could be up to 35.082~41.924 dB. Its main characteristics and function were introduced, and its application prospect was illustrated. Keywords electromagnetic environmental pollution; electromagnetic wave shielding; shielding coating; shielding effectiveness; Sn-Ni-coated glass fibre 76 引言 1 实验 为防治电磁辐射污染，采用电磁屏蔽涂料对干扰电 1.1 要原材料 子电气产品正常工作的杂散电磁波进行吸波与屏蔽处理 镍粉，其形貌如图 1 所示；镀锡镍玻璃纤维，其中含 [1-2] 、银、 是行之有效的技术途径之一 。而传统的金 铜、镍等 Sn10.11at%和 Ni0.28at% ，其形貌如图 2 所示；钛酸酯偶 金属的导电性虽好，但成本过高，极大地限制了其市场推 ；