机制砂混凝土抗氯盐侵蚀性能及结构耐久性分析-结构工程专业论文.docxVIP

等因素对不同龄期混凝土氯离子表观扩散系数的影响，提出了基于双控制 等因素对不同龄期混凝土氯离子表观扩散系数的影响，提出了基于双控制 线的混凝土氯离子扩散系数快速分析方法，建立了机制砂混凝土氯离子表 观扩散系数的多因素模型，研究表明，在浸泡试验条件下，粉煤灰和矿粉 掺量仍是影响机制砂混凝土抗氯盐侵蚀性能的最主要因素； (3)开展不同试验方法条件下机制砂混凝土抗氯盐侵蚀性能的相关性 分析，建立电场加速条件下和浸泡条件下机制砂混凝土抗氯盐侵蚀性能相 关关系模型，研究证明了经两种试验方法分析得到的抗氯盐侵蚀性能间具 有较好的线性相关关系； (4)建立了不同试验方法下基于机制砂混凝土抗氯盐侵蚀性能的氯盐 环境下混凝土结构耐久性分析模型和服役寿命预测方法，并开展了氯盐环 境下混凝土结构耐久性分析和服役寿命预测，研究结果表明，直接使用传 统服役寿命计算模型会过高估计混凝土的服役寿命，使用修正模型得到的 混凝土结构服役寿命计算模型可以更准确地评估氯盐环境下混凝土结构的 耐久性。 关键字：混凝土；机制砂；抗氯盐侵蚀性能；多因素模型；氯离子扩散系 数；服役寿命；耐久性分析 万方数据 THE THE RESISTANCE TO CHLORIDE ION PERMEABILITY AND DURABILITY PERFORMANCE ANALYSIS OF MANUFACTURED—SAND CONCRETE STRUCTURES Abstract With gradually reducing of useable natural sand in our country，the manufactured。sand will be inevitably selected as fine aggregate used in concrete． However the representation form of chlorine penetration resistance of manufactured-sand concrete under different test conditions and methods performs differently，then the analysis content of chloride diffusivity based on this is not consistent．With the related performance of anti．chloride COlTosion ability of manufactured—sand concrete under conditions of accelerated electric field and immersion test，the anti．chlorine erosion tests of accelerated electric ●● field and Immersion have been done and colTelational analyses have been promoted on the basis of different test conditions．So as the durability of manufactured-sand concrete under chloride environment． The main content and achievements of this paper are as follows： (1)The anti—chlorine erosion experiments of manufactured．sand concrete under accelerated electric field conditions have been launched and the effect of water-binder ratio，the combination of slag and fly ash，and the replacement rate of mechanism sand and coarse aggregate for anti．chlorine erosion ability of concrete has been studied．At the same time，the multi—factor model about electric flux and chloride ion diffusion coefficient data have been established and this paper has presented a cor