道路混凝土耐久性的研究 毕业论文.docVIP

PAGE 1 PAGE I 道路混凝土耐久性的研究 Study on durability and application of road high performance concrete 摘要 从耐磨性、干缩、抗裂性等方面，研究了粉煤灰、矿渣两种矿物掺合料对道路高性能混凝土性能的影响，并初步探讨了其影响机理。研究结果表明：掺人质量分数为20％一40％粉煤灰和矿渣的道路高性能混凝土具有工作性好、后期强度高、耐磨、低收缩以及抗裂性好等特点。工地应用表明，用粉煤灰与矿渣复合双掺配制的道路高。 关键词： 粉煤灰；矿渣；道路混凝土；耐久性；应用 Abstract：The efects of two minerals admixtures of fly ash and slag on road high performance concrete is studiod through the aspects of abmsion resistance，drying shrinkage，cracking resistance and so on．At the same time，the mechanism of action was analyzed and discussed．The research results showed that road high performance concrete added 20％--40％ by mass of fly ash and slag have good workability，higher later strength，beaer characters of abrasion resistance，lower drying shrink age，anti-cracking and so on．The results of application indicated that high performance concrete mixed with fly ash and slag can significantly improve the pavement performance． Key Wrrds： fly ash；slag；road concrete；durability；application TOC \o 1-3 \h \u HYPERLINK \l _Toc8865 摘要 PAGEREF _Toc8865 I HYPERLINK \l _Toc8234 第一章 绪论 PAGEREF _Toc8234 - 1 - HYPERLINK \l _Toc16663 1.1 混凝土的应用与发展概述 PAGEREF _Toc16663 - 1 - HYPERLINK \l _Toc20772 1.1.1 高性能混凝土的技术特点及要求 PAGEREF _Toc20772 - 1 - HYPERLINK \l _Toc18993 1.1.2 高性能混凝土在国内外工程中实际的应用 PAGEREF _Toc18993 - 1 - HYPERLINK \l _Toc7779 1.1.3 高性能混凝土存在的问题以及今后的发展趋势 PAGEREF _Toc7779 - 2 - HYPERLINK \l _Toc29421 1.2 现代混凝土的特点 PAGEREF _Toc29421 - 2 - HYPERLINK \l _Toc5211 1.2.1 现代混凝土配合比设计方法 PAGEREF _Toc5211 - 3 - HYPERLINK \l _Toc23458 1.2.2 化学外加剂与胶凝材料的相容性 PAGEREF _Toc23458 - 4 - HYPERLINK \l _Toc10506 1.2.3 矿物掺合料的合理使用 PAGEREF _Toc10506 - 4 - HYPERLINK \l _Toc9544 1.3 其他特种材料的应用 PAGEREF _Toc9544 - 5 - HYPERLINK \l _Toc22682 1.4 混凝土强度浅析 PAGEREF _Toc22682 - 6 - HYPERLINK \l _Toc1586 第二章 道路混凝土耐久性的实验性研究 PAGEREF _Toc1586 - 10 - HYPERLINK \l _Toc10167 2.1 原材料与试验方法 PAGEREF _Toc10167 - 10 - HYPERLINK \l _Toc368 2.1.1 原材料 PAGEREF _Toc368 - 10 - HYPERLINK \l