混合稀土阻燃镁合金ZM5表面张力及其对阻燃性能影响研究材料加工工程专业论文.docxVIP

重庆大学硕士学位论文英文摘要 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV formula of oxidation film rupture. The results indicated that RE was adsorbed in interface between melt and oxidation film，which participated in the oxidation reaction and improved the density of oxidation film that was benefited to form protective oxidation film; Besides, RE could increase the thickness of interface reactive layer and reduce the interfacial tension to make the oxidation film hard to break. RE was also by way of changing the orientation of solid-liquid interface to increase the adhesion between oxidation film and molten metal. Key