耐热粉末铝合金成形工艺研究.pdf

耐热粉末铝合金成形工艺研究 李 　伟 　　杨 　俊 　　罗琴英 ( ) 　北京机电技术研究所 　北京 　100074 　 文 　摘 　为研制超音速飞行器所需的耐热铝合金管材 ,采用喷射沉积管坯 →挤压成厚壁管材 →旋压成 薄壁管的成形工艺路线 ,旋压出Al - 8. 5Fe - 1. 3V - 1. 7Si 耐热粉末铝合金 Φ 153 mm ×1. 2 mm ×540 mm 的 内 小直径管材和 Φ 380 mm ×2 . 5 mm ×1 140 mm 的大直径管材 。大直径管材做成的模拟舱段通过了静强与静 内 热联合试验 。 关键词 　耐热粉末铝合金 ,快速凝固 ,喷射沉积 ,挤压 ,旋压 Forming Technology of Heat Resistant Powder Aluminum Alloy Li Wei 　　Yang Jun 　　Luo Qinying ( 　Beijing Electromechanical Technology Institute 　Beijing 　100074 　) Abstract 　To develop heat resistant powder aluminum alloy tubes for supersonic aircrafts , spray shaping , squeezing and spinning processes are employed respectively . Some Al8. 5Fe1. 3V1. 7Si alloy tubes are obtained with small diame ter tube of Φ 153 mm ×1. 2 mm ×540 mm and large diameter tube of Φ 380 mm ×2 . 5 mm ×1 140 mm. Simulation in in cabin made by the large diameter tubes has passed the combined thermalstatic load tests. Key words 　Heat resistant powder aluminum alloy ,Rapid solidification ,Spray shaping ,Squeezing ,Spinning 1 　前言 2 　耐热粉末铝合金成形工艺探索 随着飞行器向着超音速方向发展 ,要求材料能 要提高铝合金的耐热性能 ,必须在铝中加入过 耐 350 ℃以上高温 , 普通铝合金 已不能满足要求 。 渡族元素 Fe 、Mo 、V 、Cr 、Zr 等 ,形成热稳定的金属间 钛合金虽能够满足高温使用要求 ,但是钛合金成本 化合物 。采用常规铸锭冶金方法 ,上述元素加入量 ( ) 高 、密度相对较大且加工困难 。另外 ,在 350 ℃左右 有限。采用快速凝固/ 粉末冶金 RS/ PM 技术则可 使用钛合金有些大材小用 ; 因此开展了能在 350 ℃ 扩大这些元素的固溶度 ,形成高