毕业论文：《用旋转流变仪表征聚合物-无机填料体系相容性》.doc

PAGE 用旋转流变仪表征聚合物/无机填料体系相容性 摘 要 在小应变条件下进行的动态流变测试，不会对材料本身结构造成影响或破坏，并对材料形态结构变化十分敏感，可以准确反映多相聚合物体系组分间的相互作用和形态结构的变化。本课题研究了聚丙烯/碳酸钙体系的相容性对材料动态流变性能的影响。结果表明：对于聚丙烯/碳酸钙体系的复数粘度和储能模量,在体系的相容性较好时，随着填料的含量增加，粘度和储能模量都逐渐上升。当相容性变差时，粘度和储能模量都出现下降的现象。体系的损耗模量，损耗角在体系相容性发生变化时，受到的影响不是很大，因此在表征体系相容性方面这两个参数作用不大。 关键词： 聚丙烯，碳酸钙，动态流变性，相容性 Characterize the compatibility of polymer/inorganic packing system by using rotating rheometer Abstract The dynamic rheological tests are believed to be an effective method for obtaining the information on structure change related to thermo-stability and the evolution of morphology. The influence of the compatibility of the PP/CaCO3 to the dynamic rheological properties was studied. The results show that： for the complex viscosity and storage modulus of the PP/CaCO3 system ,when the compatibility of the system is better, with the increase of the filler content, Viscosity and storage modulus increased gradually. When the compatibility become bad, viscosity and storage modulus are declining. When the compatibility of the system is change, the loss modulus, loss angle don’t have much affected. So they have little effect on characterize the compatibility. Key words: Polypropylene ，Calcium carbonate ，Dynamic rheology， Compatibility 目 录 TOC \o 1-3 \u 1 引言 h 1 1.1聚丙烯发展简介 h 1 1.2本课题现阶段国内外发展现状 h 2 1.3流变学原理简介 h 3 1.3.1基本流变参数 h 3 1.3.2理想固体与液体的性质 h 4 1.3.3 聚合物材料的粘弹性质 h 5 1.3.4经典的线性粘弹理论 h 7 1.3.5 多相聚合物体系的粘弹理论模型 h 9 1.3.6 多相聚合物体系长时松弛与结构关系 h 10 2 实验部分 h 12 2.1实验原料 h 12 2.2实验设备 h 12 2.3 样品制备 h 12 2.3.1样品组分 h 12 2.3.2制备方法 h 13 2.4表征与测试 h 14 2.4.1 使用旋转流变仪对材料的动态流变性进行测试 h 14 2.4.2 使用扫描电镜对样品进行观测 h 14 3 结果与讨论 h 15 3.1 测量数据简介 h 15 3.2体系相容性对碳酸钙/聚丙烯体系复数粘度的影响 h 15 3.3体系相容性对储能模量（）、损耗模量（）的影响 h 18 3.3.1相容性对储能模量（）的影响 h 18 3.3.2相容性对损耗模量（）的影响 h 21 3.4相容性对损耗角的影响 h 24 4 结论 h 26 参考文献： h 27 致 谢 h 29 1 引言 1.1聚丙烯发展简介 由于聚丙烯质轻，综合性能优良，应用范围广，且生产原料易得，价格低廉，因此是主要的通用高分子材料之一。其优异的性价比在市场上极具竞争力，消费量逐年上升，全球PP生产能力由1999年的3100万吨增至2004年的4110万吨，20