基体激光淬火对镀铬层界面剪切强度的影响-中国表面工程.PDF

19 6 Vol.19 No.6 2006 12 CHINA SURFACE ENGINEERING December. 2006 6 25 * 1,2,3 1 1 1 1,3 1. 100080 2. , 255000; 3. , 100080 TN249 TG156.99 A 1007–9289(2006)06–0025–04 Effect of Laser-quenched Substrate on Interfacial Shear Strength of Chromium Plated Coatings ZHANG Guo-xiang 1,2,3CHEN Guang-nan 1ZHANG Kun 1LUO Geng-xing 1LI Huai-xue 1,3 (1.Institute of Mechanics, China Academy of Sciences, No.15 Beisihuanxi Road, Beijing , China 100080; 2. ShangDong University of Technology, Zibo ShangDong, China 255000; 3. Graduate School of China Academy of Sciences,Beijing, China. 100080) Abstract: Directing against the real working condition of Cr-plated gun bore, the laser-quenching of substrate was adopted. It was indicated by multi-cracks tensile method that the interfacial shear strength was greatly increased, its service life could be obviously improved, and the mechanism was discussed from the materials science. The interfacial strength was evaluated by ion peening technology ,the result showed that laser quenching substrate could not only eliminate interlayer between substrate and Cr-coating but also increase the strength of materials near interface. The mechanism of improving strength was due to the refined grain of Cr-coatings interface. Key words: interfacial shear strength; chromium-plated coatings; laser quenching substrate; strength of materials 0