离子交换法制备钠钙硅高强单片防火玻璃的研究-材料学专业论文.docxVIP

摘 摘 要 Abstract With the rapid development of high—rise buildings in cities，people bring forward that building glass should sarisfy with the fire—resistant and adiabatic criterion．At present，because the accident of conflagration happened in row,the demand for fire resistance is rising．The developed industry countries laying their emphases researching and producing for the safety fire·resistant materials． Fire—resistant glass is the special glass that Can keep integrality and heat insulation under the condition of fire—enduring experimentation．The fire-resistant glass consists of single and compound glass according the structure．The compound fire·resistant glass is the special glass that is compounded by two several layer glasses，or single panel and organic materials，which satisfies with the fire—resistant rate．But compound fire—resistant glass is lack oftransparence and climate—resistant． With various modem architecture coming forth，such as exhibition，gymnasium， trade high—rise，people’S house and on．More and more people pay attention the beauty，practicability,security of the architecture．The single panel fire—resistant glass represents new functional glass material，compared with the compound glass，it has the high transparence ratio，high mechanical properties and it is easy install．So it is applied in many places，such as outside wall，fire—resistent partition，fire—resistant window,door and In this study,the preparation of the NCS float single panel fire—resistant glass with ion—exchange means was studied．The ralationship and influence between the molten salt component，the ion—exchange system，the ion—exchange depth and the properties were researched by EPMA，XPS，the of microhardness，bending strength，surface and light transmittance．Effect of Cs+content properties of Ion·exchanged NCS Glass was research in em【phases．The molten salt component and the ion—exchange technics were determined by experiment，then the single panel fire—resistant glass with the high mech