水性聚氨酯研究二续-Core.pdf

综 　　述　　　　　　　　　　　　　　　　　　　　　　　　　　　　粘 　接 　200 1 , 22 ( 2) ( ) ( ) 水性聚氨酯研究 二 续 周善康 　许一婷 　林健青 　戴李宗 (厦门大学材料科学系 ,厦门市 361005) 摘要 　较系统地阐述了关于水性聚氨酯研究的各个方面 ,包括其基本概念 ,研究开发背景 ,制备原理 、方法和 　　 工艺 ,产物液体和胶膜的物理性能及其影响因素 , 以及应用领域等 。并阐明了自乳化历程 ,乳液稳定机制 。 关键词 　水性聚氨酯 　制备 　物理性能 　应用领域 ( ) The study of water borne polyurethane Ⅱ Zhou Shankang 　Xu Yiting 　Lin Jianqing 　Dai Lizong (Department of materials science of Xiamen University ,Xiamen 361005) Abstract 　These papers reviewed systematically on the various aspects of the study of water borne polyurethane , and expatiate emphatically on the preparative theories ,methods and technics ,the physical performances and influential fac tors of productions and their cast films. Furthermore , the R D background , self emulsifying process , stabilization mechanism of dispersion and the application fields are also introduced. Keywords 　Water borne polyurethane 　Preparative method 　Physical performance 　Application films 4 　物理性能及其影响因素 个成分含量的增大所造成的聚合物链刚性增大的约 聚氨酯离聚物是含有交替软硬链段单元并带有 束[15 ] 。同时 ,粒径随软段分子质量的增大而减小还 少数被中和成盐的羟基和叔胺基侧链的嵌段共聚 与 PU 链段的柔韧性增加有关 ;柔韧性可改善乳胶 物 。软段通常由聚醚或聚酯多元醇组成 ,硬段则由 粒子变形性 ,使液体粘度降低 ,有利于分散相更好破 异氰酸酯扩链形成 。PU 离聚物的性能主要取决于 碎 ,形成更小粒子 。当粒径的减小主要是由亲水性 软硬链段的相互行为和离子的种类 ,特别是不相容 的增加引起时 ,随溶胀的增加一般可得到一个平衡 的软段链区和硬段链区之间的微相分离[29 ] 。微区 粒径 。 形成的潜在驱动力是氨基甲酸酯键与脲基之间的氢 聚多元醇的链段结构也对 PU 软硬段的相混有 键和来自羧酸离子基团之间的静电力即库仑力 , 以 [32 ] ( ) 重要影响 ,如就聚四氢呋喃 PTHF 和聚丙二醇 及硬段相和软段相中可能存在的结晶[30