闭挤式精冲成形材料流动及变形区显微状态分析.pdfVIP

摇摇摇 58 精 密 成 形 工 程摇 摇 摇 2010年1月 闭挤式精冲成形材料流动及变形区显微状态分析 陈明明,邓明,吕琳,杨显红 (重庆理工大学材料工程学院,重庆400050) 摘要:通过对闭挤式精冲零件进行金相观察,变形区流线和显微硬度分析,对闭挤式精冲加工中出现的 一些材料微观状态的特点和规律进行了研究。 关键词:精冲;成形机理;显微硬度 中图分类号:TG381摇 摇 摇 文献标识码:A 文章编号:1674鄄6457(2010)01鄄0057鄄04 Research on Flow Mechanism of Materials and Micro鄄state of Distortion Area in Closed Extruding Fine鄄blanking Process CHEN Ming鄄ming,DENGMing,LVLing,YANGXian鄄hong (Chongqing University of Technology,Chongqing400050,China) Abstract:There are some differences between traditional fine鄄blanking and closed extruding fine鄄blanking in stress,separation process and the changes of materials performance. By metallographic observation and analyzation of flow line of deformation zone and microhardness of the closed extruding fine鄄blanking parts,the characteristics and rules of the micro鄄state of materials in closed extru鄄 ding fine鄄blanking process are researched. Key words:fine鄄blanking;forming mechanism;microhardness 摇 摇 闭挤式精冲通过在变形过程中始终将坯料限制 在有限的模具型腔内,使变形区产生比强力压边精 冲更强大的静水压力,提高变形区材料的塑性,可以 达到精冲低塑性材料和厚板的目的。 用该闭挤式精 冲工艺对材料为硬铝 LY12 的坯料进行加工,得到 了具有较高表面质量的精冲制件(如图1所示)。 该零件尺寸公差可达IT8~7级,剪切面粗糙度可达 [1] 0.8~0.4 滋m 。 在此,对闭挤式精冲工艺的变形 图1摇 闭挤式精冲零件 分离过程、应力状态和精冲件的组织性能变化,以及 Fig.1摇 Part of closed extruding fine鄄blanking 显微硬度分布等方面进行实验研究,对于促进这一 新工艺的应用很有意义。 收稿日期:2009鄄11鄄27 基金项目:重庆市科委攻关项目(CSTC,2007AC3032) 作者简介:陈明明(1984-),男,重庆云阳人,硕士研究生,主要从事精冲方面的研究。 第2卷摇 第1期摇 摇 陈明明等:闭挤式精冲成形材料流动及变形区显微状态分析 摇摇摇 59 1摇 实验方案 实验所用材料为硬铝 LY12,该合金精冲性较 差,测得延伸率啄=9.5%,在相关资料中给出的精冲 [2] 适应性为3,属于精冲困难的材料 。 实验中首先 将待分析的零件沿直径剖开,如图2所示,左边为成