整体浇筑长大混凝土结构养护期间早期开裂问题探讨.pdf

整体浇筑长大混凝土结构养护期间早期开裂问题探讨 　　程宝辉 69 ( ) 文章编号 :1003 - 4722 2004 03 - 0069 - 04 整体浇筑长大混凝土结构养护 期间早期开裂问题探讨 程宝辉 ( 中铁大桥局集团桥科院 ,湖北 武汉 430034) 摘　要 : 整体浇筑已成为长大结构重要的施工方法之一 ,但结构养护期间的早期开裂问题也 日益凸现。在分析引起早期开裂影响因素的基础上,结合工程实例进行了详细的理论计算 ,对整体 浇筑长大结构的施工及制定养护工艺具有一定的指导意义。 关键词 : 温度应力 ;养护 ;收缩 ;水化热 ;裂缝 中图分类号: U448. 38 文献标识码 : A Study of Initial Cracking Problems of IntegrallyCast Long and Large Concrete Structures During Curing Period CH EN G Baohui (Bridge Science Research Institute Ltd., China Zhongtie Major Brid ge Engineering Group , Wuhan 430034 , China) Abstract : The integral casting of concrete becomes one of the important construction methods of long and large structures. However , the initial cracking of the structures during their curing period is a problem that is increasingly significant . In this paper , based on the analysis of the factors that may cause influences upon the cracking , and with reference to several projects , the detailed theoretic calcu lations in connection with the cracking are made , which may serve as certain guidance to the construc tion of the structures and to the formulation of their curing technology. Key words : temperature stress ; curing ; shrinkage ; hydration heat ; cracking 1 　概 　述 同普通混凝土相比 ,高性能混凝土具有以下特 整体浇筑 、运输、拼装已成为长大结构重要的施 点 : ①水泥标号更高 ,掺入了大量的高细度矿物掺 工方法之一 ,但其早期开裂问题也日益凸现。特别 合料 ; ②水胶比小 , 水泥浆体积的相对含量高 ; ③ 是采用高性能混凝土的整体浇筑长大结构 ,早期开 水泥水化快 ,水化结束得早 ; ④水泥石结构密实 ,总 裂问题较普通混凝土结构更加突出。水平基础上整 孔隙率